Experimental study on bond behavior between corroded rebar and steel fiber reinforced concrete

HOU Lijun,LIU Hong,XU Shilang,CHEN Da

DOI: https://doi.org/10.14006/j.jzjgxb.2017.07.018

2017-01-01

Abstract:Steel fiber reinforced concrete (SFRC) has been used in retrofitting and strengthening of engineering structures extensively,depending on fine tension properties after cracking and toughness.In the case of corroded members repaired using SFRC,the bond behavior between corroded rebar and SFRC is a key factor for the mechanical properties of repaired members.In the present study,an electrolyte corrosion technique was firstly used to accelerate steel rebar corrosion,and then the corroded rebar was cleaned up and used for pullout specimens,and finally the bond behavior of corroded rebar and SFRC was studied through central pull-out test.The experimental results indicate that the addition of steel fiber can transform the splitting failure to pullout failure mode,and the bond strength ratio increases by 4.4％-7.5％.With the decrease in bond length,the relative slip between loading and free ends decreases whereas the average slip at the peak bond stress increases.The influence of corrosion ratio on the bond strength of reinforcement and SFRC is related to the bond length.When the corrosion ratio increases to about 15％,the bond strength decreases by 21％ for specimens with bond length 3d (d is diameter of reinforced rabar),while the bond strength almost remains a constant for specimens with bond length 7d.Based on the experimental results,an empirical equation,considering corrosion ratio and bond length,is proposed for predicting the bond strength,and the calculated result agrees well with the tested value.