Oxidative Degradation of Tetracycline Hydrochloride Using Nano Fe∕Co Alloy and H2O2under Fenton Conditions

Junchao LI,Jinyuan JIANG,Wei ZHANG,Lu BAI,Yun LI,Chunlian XU

DOI: https://doi.org/10.13198∕j.issn.1001-6929.2018.01.10

2018-01-01

Abstract:In order to investigate the Fenton-like catalytic activity of nano Fe∕Co alloy to wastewater which contained tetracycline hydrochloride (TCs),and the effects of pH,H2O2,active ion leaching and other factors on the catalytic activity, the nano Fe∕Co alloy was prepared using liquid reduction method. In addition,we explored the Fenton-like catalytic properties, the leaching amount of Fe and Co,and the relationship between changes in structural surface area and catalytic activity.Under the conditions of adding nano Fe∕Co alloy, the influences of system pH value,H2O2additions and initial TCs concentration on the catalytic degradation efficiency of TCs were studied using single factor analysis. The results showed that: (1) In the preparation of nano Fe∕Co alloy, the additions of polyvinyl pyrrolidone (PVP) could effectively prevent the agglomeration of nano Fe∕Co alloy and promote the increase of specific surface area of nano Fe∕Co alloy (BET=113.8 m2∕g). (2) Nano Fe∕Co alloy had the advantage in widening pH use range in the catalytic system. At pH=3.0-9.0 range,the removal efficiency of nano Fe∕Co alloy (87.2%-91.7%) to 30 mg∕L TCs solution was greater than those of FeCl2(0-30.7%) and nano Fe (0-28.2%). The removal rate of TCs (86.2%) was the best as the addition of H2O2exceeded 150 mmol∕L. (3) For the nano Fe∕Co alloy catalytic system(pH=3.0-11.0), the leaching concentrations of Fe and Co were 0.20-0.35 mg∕L and 0.20-1.00 mg∕L respectively,meeting the requirements of GB 3838-2002 'Environmental Quality Standards for Surface Water', long-term use will not result in a large accumulation of leaching components (Fe, Co) in the environment, potentially reducing the potential risks to the ecological environment;(4) Nano Fe∕Co alloy had reusability,and the degradation of TCs was still above 50.0% after 4 times of catalytic utilization. In conclusion, the nano Fe∕Co alloy had higher catalytic performance and reusability for degradation of TCs, and the advantages in broadening the use of catalytic system pH range,with the stability of the active ingredient Fe,Co concentration advantage.