Experiment of Wood Vinegar Produced from Pine Nut Shell Continuous Pyrolysis.
Jiang Enchen,Zhao Chenxi,Qin Liyuan,Chen Aihui
DOI: https://doi.org/10.3969/j.issn.1002-6819.2014.05.033
2014-01-01
Abstract:With China’s growing energy problems, biomass conversion technologies have attracted considerable attention for converting biomass into energy products. These technologies can be divided into four main categories: direct-combustion processes, thermochemical conversion, biochemistry and liquefaction technology, respectively. Of the variety of technologies, thermochemical conversion and, particularly, pyrolysis have aroused great attention all over the world in recent years. Biomass as a renewable energy source has significant potential to transform into high-value and high-grade charcoal, bio-oil and combustible gas by the pyrolysis process. The wood vinegar refined from pyrolysis bio-oil can be used as insect repellents, plant growth-promoting liquid fertilizer, and as a soil improver after appropriate treatment, which has a very broad market prospects. The use of wood vinegar presents some problems due to its complex ingredients and big quality differences obtained by different materials and process conditions. However, there are very limited studies on the produced conditions and properties of biomass pyrolysis wood vinegar.In this paper, red pine nut shell, which is a specialty in the northeast of China, was pyrolysed as raw material. The characteristics of wood vinegar have been investigated, including proximate analysis, elemental analysis, composition analysis, heating value analysis and thermo-gravimetric analysis (TGA). The experiments were conducted on the biomass continuous pyrolysis reaction device with a variable pitch spiral conveyor to obtain wood vinegar at different reaction temperatures (300℃,400℃, 500℃600℃and 700℃) and different reaction times (4min、6min、8min、10min and 12min). The characteristics of wood vinegar consisting of water content, viscosity, pH value, chemical compositions, the antioxidant activity and corrosion properties were determined by the Karl Fischer method, viscometer, acidity meter, gas chromatography and mass spectrometry (GC-MS), ultraviolet spectrophotometer, and scanning electron microscope (SEM), respectively, which provided a scientific basis for the study of the pine nut shell pyrolysis process.The results were as follows:with pyrolysis temperature increasing, the yield of wood vinegar increased gradually until the temperature reached 500 ℃, which provided the maximum yield, then reduced quickly. The moisture content of wood vinegar gradually decreased from about 94% to 85%; the viscosity decreased gradually; the liquidity became stronger; and the pH showed a slow decreasing trend, from 3.2 down to about 2.6. With increased pyrolysis time, the yield of wood vinegar had no significant change, water content basically appeared as an inconspicuous trend, the viscosity showed almost no obvious trend, the liquidity also almost had no significant change, and the pH ranging of wood vinegar made little change by contrast. In addition, the main ingredients of wood vinegar were phenols, ketones, ethers, esters, aldehydes, acids, alcohols and amines at a pyrolysis temperature of 500℃and a pyrolysis time of 8min, in which the contents of phenols and ketones were 53.88%and 20.93%, respectively. Under the same pyrolysis conditions, the hydroxyl radical scavenging rate of wood vinegar was 66.63%, equivalent to 3μmol/L of ascorbic acid. SEM images showed that wood vinegar had a significant role in scavenging hydroxyl free radicals, which had a strong antioxidant activity. Wood vinegar gained under the condition of 500℃and 8min had weak corrosion, despite the low pH value of 3.1. All of the above results provided a theoretical basis for experimental study of wood vinegar prepared from pine nut shell continuous pyrolysis.