Synthesis and process optimization of lignosulfonate graft copolymer
Rui GUO,Bo SONG,Yu GUO,Yunpeng LI,Ruixiang TU,Yingyue WANG,Lan MA
DOI: https://doi.org/10.16085/j.issn.1000-6613.2017-1304
2018-01-01
Abstract:Using the lignosulfonate,the sodium methacrylate and the allyl polyoxyethylene ether as raw materials,the potassium persulfate as initiator,the lignosulfonate graft copolymer(LS-SMAS-APEG) was synthesized by aqueous solution polymerization. The chemical structure of the product was characterized by infrared spectrum(FTIR)and environmental scanning electron microscope(ESEM). The effects of monomer dosage,temperature,reaction time and K2S2O8dosage on apparent viscosity were investigated. Furthermore,based on the single factor experiment,the technical parameters of grafted lignosulfonate were optimized by using the orthogonal test. The results indicated that the optimal conditions for the preparation of grafted lignosulfonate were as follows:reaction temperature 75℃, reaction time 4h,initiator dosage 4%,the sodium octyl methane sulfonate dosage 20%,the allyl polyoxyethylene ether dosage 35%. And the effect of the apparent viscosity of the slurry intrinsic viscosity and zeta potential test on the LS-SMAS-APEG dispersant was investidagted. The test results showed the effectiveness of viscosity reduction,dispersion and stabilization to the Shenhua coal.