Preparation of PLA/PCL Blend and Its Application on Medical Materials

Fanwen Yang,Yongliang Lin,Xiumei Tian,Xiaoming Chen,Ye Peng,Jixiang Zhu,Mian Wu,Xinyue Huang

DOI: https://doi.org/10.3969/j.issn.1001-3539.2014.02.001

2014-01-01

Abstract:Polylactic acid (PLA)/polycaprolactone (PCL) blend was prepared by melt process and the effect of PCL content on process properties and mechanical properties of the blend were investigated. The result show that melt torque and balance torque of the blend decrease in general with the increase of PCL content in the process of blending,tensile strength decreases,the elongation at break first increases and then decreases,reaches maximum when the mass fraction of PCL is 30%. Impact strength first increases fastly, then slowly when mass fraction of PCL is more than 30%. On this basis,the tendon anastomosis was prepared with PLA/PCL blend by ultrasonic welding technology. The effects of pressure and rolling speed on appearance quality of the anastomosis were studied based on PLA/PCL (70/30) blend. Under the pressure of 2.0 MPa and the rolling speed of 5 mm/s,the tendon anastomosis with good shape and satisfactory hole quality was prepared. Then,the sewing properties of the tendon anastomosis prepared by the blends with different PCL content were investigated under the process conditions mentioned above. The results indicate that the tendon anastomosis prepared with PLA/PCL (70/30) blend was characterized with good flexibility and difficult pulling in vitro simulating sewing process,which shows a good application prospect in surgical operation field such as tendon repair.