Tribological Properties of Surface Nanocrystallized 316L Stainless Steel Under ZDDP Lubrication

WANG Yanyan,YUE Wen,SHE Dingshun,FU Zhiqiang,HUANG Haipeng,LIU Jiajun

DOI: https://doi.org/10.3969/j.issn.1001-8719.2016.02.010

2016-01-01

Abstract:T he tribological properties of 316L stainless steel processed by ultrasonic surface nanocrystallization were investigated by a SRV tribometer under PAO4 and ZDDP lubrications .The microstructural evolutions of the nanocrystallized sample were characterized by X‐ray diffraction (XRD) and optical microscope .The morphologies of the wear surfaces and chemical composition of tribofilms were investigated by scanning electron microscopy (SEM ) and X‐ray photoelectron spectroscopy (XPS) ,respectively .The results showed that ultrasonic surface nanocrystallization treatment could significantly improve the hardness of 316L stainless steel .The micro‐dimples on the nanocrystallized surface might play a role as lubricant reservoirs ,thus the friction‐reduction and anti‐wear properties of nanocrystallized sample were much better than those of the original sample under PAO4 lubrication . The wear resistance of the nanocrystallized sample was remarkably improved under PAO4 + ZDDP lubrication , which was attributed to the formation of a polyphosphate tribofilm with shorter chain length and the higher contents of Zn and P in the tribofilm on the nanocrystallized surface ,thus the adhesive wear was reduced significantly with obvious enhancement of anti‐wear properties .