Exploring influence of MgO/SiO 2 on viscosity-temperature property of coal ash slags under entrained flow gasification condition
Meng Li,Hao Wu,Jianliang Xu,Guangsuo Yu,Xueli Chen
DOI: https://doi.org/10.1016/j.energy.2023.129033
IF: 9
2023-10-09
Energy
Abstract:To realize smooth slag discharge of Zhundong coals in entrained-flow-bed gasifier, the viscosity-temperature characteristics of slags with different MgO/SiO 2 ratios were studied. The results show that low MgO/SiO 2 ratio causes high BO content in liquid slag, resulting in excessive polymerization degree and viscosity. As the MgO/SiO 2 increases, the activation energy of liquid slag increases, occurrence form of oxygen transforms from BO to NBO, more structural depolymerization reactions occur, and [SiO 4 ] tetrahedra obtains more O 2− and show more NBO. NBO is more likely to react with Mg 2+ , Ca 2+ , Al 3+ , and Fe 2+ to form crystals, thus increasing the crystallization reaction activity of slag and cause the initial crystallization temperature and crystal content increasing. An increasing MgO/SiO 2 causes a characteristic transition of slag from weak crystallinity and high polymerization degree to strong crystallinity and low polymerization degree, meanwhile, the poor viscosity-temperature characteristics with high viscosity of liquid slag is first improved, and then the problem of strong crystallinity leading to poor viscosity-temperature characteristics with high T cv occurs. Therefore, the viscosity-temperature characteristics first improve and then deteriorate. The crystal size increases as MgO/SiO 2 increases, which also cause T cv increasing. Large Δ T and low T p25 make 0.28MS become the most suitable for slag discharge.
energy & fuels,thermodynamics