Abstract:To avoid the "susceptibility artifacts" in magnetic resonance imaging (MRI) and realize patient-specific medical devices with complicated shapes, a novel MRI compatible Zr-1Mo alloy with low porosity (c.a. 0.4%) were manufactured by laser powder bed fusion process(L-PBF) using gas-atomized Zr-1Mo(wt%) alloy powder. However, as-built Zr-1Mo(wt%) components using optimized process parameters show relatively high me-chanical performance(elongation of 6.4%, UTS of 1175 MPa), but contain 0.4 vol% defects which show a spherical morphology and distribute in the builds randomly. These defects definitely deteriorate the mechanical performance(especially ductility, fatigue behavior) of Zr-1Mo components manufactured by L-PBF. In order to eliminate defects in as-built Zr-1Mo components, hot isostatic pressing(HIP), which has been known as an effective process to decrease the porosity of additive manufactured products, was executed. Due to the elevated temperature and high pressure during HIP treatment, the randomly distributed defects were eliminated after the HIP process. Moreover, the alpha-martensite structure in the as-built alloy was transformed into a basketweave alpha + beta structure at low HIP temperature(1023 K and 1073 K) or lamellar alpha + beta structure at relatively high HIP temperature(1173 K and 1273 K). In the meantime, the elongation of HIP-treated Zr-1Mo components significantly increased, but the strength shows the opposite trend. From the viewpoint of mechanical property, Zr1Mo components HIP-treated at 1023 K possessed elongation of 19.9%, and UTS of 628 MPa should be optimized in this study. More importantly, porosity regrowth behavior was investigated to evaluate subsequent heat treatment feasibility for further improvement of mechanical performance. Due to intact raw material power as well as vacuum/low pressure inside the original defect caused by evaporation of metals, porosity regrowth can not be confirmed in HIP-treated Zr-1Mo components after subsequent heat treatment(holding temperature higher than the beta transus of Zr-1Mo alloy). Therefore, further improvement of mechanical performance by subsequent heat treatment for HIP-treated Zr-1Mo components is very promising and should conduct further research in the future

Influence of Annealing Treatment on the Microstructure, Mechanical Performance and Magnetic Susceptibility of Low Magnetic Zr–1Mo Parts Manufactured Via Laser Additive Manufacturing

Microstructure, Compressive Performance and Wear Resistance of Pure Molybdenum Additively Manufactured Via Laser Powder Bed Fusion

Effects of Process Parameters on the Mechanical Properties of Additively Manufactured Zr-1Mo Alloy Builds.

Effects of Quenching Process on Microstructure, Mechanical Properties and Magnetic Susceptibility in Zr 1mo Alloy Fabricated by Powder Bed Fusion Process

Hot Isostatic Pressing of MRI Compatible Zr-1Mo Components Manufactured by Laser Powder Bed Fusion

Fabrication and Characterization of a Low Magnetic Zr-1Mo Alloy by Powder Bed Fusion Using a Fiber Laser

Microstructure and Mechanical Properties of MRI-compatible Zr-9Nb-3Sn Alloy Fabricated by a Laser Powder Bed Fusion Process

Combination of Hot Isostatic Pressing and Subsequent Heat Treatment for Additively Manufactured Zr-1Mo Components

Microstructure evolution and ductility improvement of additively manufactured biodegradable zinc–magnesium alloys via annealing

Microstructural and mechanical property evolution of a nuclear zirconium-4 alloy fabricated via laser powder bed fusion and annealing heat treatment

Microstructural Evaluation and Tensile Properties of Al-Mg-Sc-Zr Alloys Prepared by LPBF

Improved Mechanical Properties of Additive Manufactured Ti-6Al-4V Alloy via Annealing in High Magnetic Field

Microstructure Development of AM-fabricated Pure Zn with Heat-Treatment and Its Mechanical Properties, Degradation Behavior, and Biocompatibility

Novel MRI-compatible Zr–Mo–Nb alloys with superior mechanical performance, high corrosion resistance and good cytocompatibility for biomedical applications

Novel isotropic mechanical properties of laser powder-bed fusion Sc/Zr modified Al alloy

Influence of heat treatment on microstructure, mechanical and corrosion behavior of WE43 alloy fabricated by laser-beam powder bed fusion

Effect of Molybdenum on Microstructures in Zr-1.2Nb Alloys after Β-Quenching and Subsequently 873 K Annealing

Temperature gradient induced tough-brittle transition behavior of a high-strength Al-4.2Mg-0.4Sc-0.2Zr alloy fabricated by laser powder bed fusion additive manufacturing

A study of mechanical and magnetic properties in a metastable Zr–10Nb–6Sn alloy for MRI-compatible hard tissue replacements

The Mechanical Properties of the Mo-0.5Ti and Mo-0.1Zr Alloys at Room Temperature and High Temperature Annealing

Microstructure and Mechanical Properties of an Al–Mg–Si–Zr Alloy Processed by L-PBF and Subsequent Heat Treatments