Novel barium zirconate titanate-based lead-free ceramics with stably high energy storage performance over a broad temperature and frequency range
Xiongwei Lin,Xiaobo Zhao,Lei Zhou,Mingrui Zhao,Yi Lin,Yingbang Yao,Bo Liang,Tao Tao,Sheng-Guo Lu
DOI: https://doi.org/10.1007/s10854-021-05814-9
2021-04-04
Abstract:Lead-free relaxor ferroelectric ceramics with high recoverable energy storage density and energy storage efficiency over a broad temperature and frequency range are attractive for pulsed power capacitor applications. In this work, novel barium zirconate titanate-based lead-free relaxor ferroelectric ceramics are designed via introduction of Bi(Zn<sub>0.5</sub>Sn<sub>0.5</sub>)O<sub>3</sub> with heterovalent ion substitution at both A- and B-sites which could disrupt long-range order, induce polar nanoregions (PNRs), and reduce remnant polarization (<i>P</i><sub>r</sub>). The (1 − <i>x</i>)Ba(Zr<sub>0.15</sub>Ti<sub>0.85</sub>)O<sub>3</sub>–<i>x</i>Bi(Zn<sub>0.5</sub>Sn<sub>0.5</sub>)O<sub>3</sub> ((1 − <i>x</i>)BZT–<i>x</i>BZS) (<i>x </i>= 0.02, 0.06, 0.10, and 0.14) ceramics were prepared using a conventional solid-state reaction method. In addition, the structure, dielectric, ferroelectric, and energy storage properties of (1 − <i>x</i>)BZT–<i>x</i>BZS ceramics were systematically studied. All (1 − <i>x</i>)BZT–<i>x</i>BZS ceramics exhibited pure perovskite structure. With the increase of BZS content, the relaxor ferroelectric feature of (1 − <i>x</i>)BZT–<i>x</i>BZS ceramics tended to increase gradually, and slim linear <i>P</i>–<i>E</i> loops were obtained in <i>x</i> = 0.10–0.14. A high recoverable energy storage density <i>W</i><sub>rec</sub> of 2.16 J/cm<sup>3</sup> and a high energy storage efficiency <i>η</i> of 90.3% were simultaneously achieved in <i>x </i>= 0.10 at 250 kV/cm, together with excellent temperature and frequency stability, which were superior to those of the reported barium zirconate titanate-based ceramics. Our work provides an effective strategy to optimize the energy storage performance of lead-free barium zirconate titanate-based ceramics toward practical applications.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied