Abstract:It is well known that conductivity is one of the key parameters for HVDC cable insulation material XLPE, which determines the electric field distribution varying with temperature and field strength. In practice, XLPE insulation, especially for HVDC cable with large insulation thickness, usually exhibits certain level of radial inhomogeneity depending on morphological structure, crosslinking byproducts, and so on. In this paper, the radially distributed non-uniform conductivity in XLPE insulation of a degassed 500 kV DC cables are examined at different field stresses and temperatures. It is founded that the radial conductivity is greater in internal portion than the external portion of cable insulation, in which the variance of radial conductivity throughout the XLPE insulation is from several times to two orders in magnitude from 30 °C to 70 °C at field strength of 10 kV/mm to 50 kV/mm. The standard deviations of conductivity have been calculated from the data of different positions along the radial direction for the cable, which indicates the magnitude difference is usually greater at minor temperature. After that the distributed electric field is examined at rated and test voltage standards, under full load and no-load conditions on the basis of above results through the finite element simulation method. The maximum electric field strength for the HVDC cable insulation at no load condition is higher than that for full load condition at test voltage U0, 1.45 U0 and 1.85 U0. The conclusion drawn shows that the radially distributed non-uniform conductivity has a notable influence on the actual distributed electric stress in XLPE insulated HVDC cable.

Simulation of Insulation Electric Field of HVDC XLPE Cable Based on Radial Non-uniform Conductivity Distribution