7075 aluminum alloy Friction Stir Welding (FSW): Quality analysis and mechanical properties with WC-Co tool
Chongjun Wu,Jiaxuan Wang,Qingxia Wang,Peiyun Xia,Dongliu Li
DOI: https://doi.org/10.1016/j.mtcomm.2024.108203
IF: 3.8
2024-01-28
Materials Today Communications
Abstract:Friction stir welding (FSW) has been widely regarded as an ideal welding method for efficient aluminum welding with good quality. However, the conventional H13 steel tool can not be stably applied in long-distance and high-quality welding of high-strength 7075 aluminum alloy , which demands novel welding tool with high temperature resistance, wear resistance and fracture resistance. In this paper, a novel GU25UF alloy was chosen as the new welding tool due to its superior mechanical strength and wear resistance compared to traditional H13 steel, particularly at elevated temperatures. FSW process experiments were carried out on high-strength aluminum alloy using the GU25UF welding tool. By analyzing the forming results of the joint, the influence mechanism of heat input conditions on welding quality was detailedly revealed. EBSD test was carried out on the WNZ and the BM, the average grain size and grain boundary ratio were analyzed using IPF and KAM maps, revealing the occurrence of dynamic recrystallization in the WNZ during FSW process. Based on experimental results and characterization of fracture morphology under different welding processes , the location of the joint weak zone was determined. Moreover, it is comprehensively investigated in terms of the effect of microstructure's characteristics on the joint mechanical properties as well as failure mechanisms and fracture characteristics . The findings demonstrate that the joint properties are influenced by microstructure and material fluidity. In terms of grain strengthening mechanism, fine grain strengthening has a great impact than deformation strengthening. Moreover, the joint obtained using GU25UF alloy exhibit superior properties compared to those made with traditional H13 welding tools at low rotation speeds and welding speeds. The maximum values for the hardness in WNZ, the tensile strength and the elongation of the joint are 148HV, 492.3 MPa and 6.2%, respectively; resulting in a strength coefficient of 87.4%. Furthermore, the heat-affected zone is identified as the primary weak zone affecting mechanical properties while shear fracture occurs along a 45o direction.
materials science, multidisciplinary