Optical Transitions and Upconversion Properties of Er 3+ -Doped Chloride Tellurite Glasses

L Wen,Sg Li,Gs Huang,Ll Hu,Zh Jiang

DOI: https://doi.org/10.1088/1009-1963/13/2/023

2004-01-01

Chinese Physics

Abstract:Er3+-doped lead chloride tellurite glasses were prepared using the conventional melting and quenching method. The absorption spectra were measured and the Judd–Ofelt analysis was performed. The spectroscopic parameters such as the intensity parameters, transition probabilities, radiative lifetimes and branching ratios were obtained. Intense infrared emission and visible upconversion luminescence under 976 nm excitation were observed. For the 1.55 μm emission, the full width at half maximum and the emission cross sections are more than 50 nm and 8×10−20cm2, respectively. Three efficient visible luminescences centred at 525, 547 and 658 nm are assigned to the transitions from the excited states 2H11/2, 4S3/2 and 4F9/2 to the ground state 4I15/2, respectively. The upconversion mechanisms and the power-dependent intensities are also discussed and evaluated.