Abstract:In response to the National Development and Reform Commission's "Guiding Opinions on Comprehensive Utilization of Large Solid Wastes during the Fourteenth Five Year Plan", further expand the use of steel slag as concrete admixture in construction projects and other fields, and gradually improve the comprehensive utilization ratio, a cementitious composite with high utilization of steel slag (CHS) was developed, which is with the cement replaced by high-content super-fine steel slag powder (SSP) (replacement ratio υ ≥ 30%) as the cementitious materials, steel slag sand (SS) as the only aggregate and environmentally basalt fiber (BF) for toughening. It improves the utilization percentage of steel slag (SSP and SS) and reduces the consumption of natural resources such as cement and natural sand. Use BF to achieve better strength and toughness. In order to better understand the performance of CHS and make it better used in the engineering field. Study the influence of each component on the strength and energy consumption of compression and splitting tension, and strive to find the optimal proportion and lay the theoretical foundation for its application. Through the tests, the effects of high replacement ratio υ (30%–50%), low binder-aggregate ratio γ (0.31–0.44), and BF content ρ v (0%–2%) on the aspects of peak strength, force-deformation curve and energy consumption were analyzed. The results show that the standard curing f ck and f t,s can reach 40 MPa and 5 MPa respectively. With the increase of υ , the maximum axial compressive strength f ck and splitting tensile strength f t,s decreased insignificantly. The γ has an important influence on f ck and f t,s . When it increases from 0.31 to 0.44, f ck increases linearly by 63.1% to 40.4 MPa, while f t,s increases by 52.8% to 5.18 MPa. As ρ v increases, f ck and f t,s show a trend of first increasing and then decreasing. ρ v exerts a significant impact on the descending segments of stress-strain response curves of the compression which expressed as bilinear and trilinear models with different ρ v after normalization. The energy consumptions of peak, total, and residual ( E peak , E disp , E res ) show a slight downward trend with the increase of υ , a significantly upward trend with the increase of γ . With the increase of γ v , and E disp increase first and then tend to be flat, while E res always increases and the percentages of E res / E disp in the compressive test increase from 22.6% to 38.5%, reflecting the improvement of the compressive toughness of BF.

Preparation of Sustainable and Green Cement -Based Composite Binders with High -Volume Steel Slag Powder and Ultra Fi Ne Blast Furnace Slag Powder

Preparation of sustainable and green cement-based composite binders with high-volume steel slag powder and ultrafine blast furnace slag powder

Preparation and Hydration Properties of Steel Slag-Based Composite Cementitious Materials with High Strength

Insight into the performance of composite binder with high-volume steel slag, blast furnace slag and desulfurization gypsum

Laboratory Preparation and Performance Characterization of Steel Slag Ultrafine Powder Used in Cement-Based Materials

Preparation of steel slag-based cementitious materials compounded with GBFS and phosphogypsum: mix design, hydration, and microstructure characteristic

Recycling of steel slag powder in green ultra-high strength concrete (UHSC) mortar at various curing conditions

Hydration Superposition Effect and Mechanism of Steel Slag Powder and Granulated Blast Furnace Slag Powder

Preparation and Hydration Mechanisms of Low Carbon Ferrochrome Slag-Granulated Blast Furnace Slag Composite Cementitious Materials

Mechanical Properties and Microscopic Mechanism of a Multi-Cementitious System Comprising Cement, Fly Ash, and Steel Slag Powder

Resource utilization of solid waste from steel industries in cement-based cementitious materials: Mechanical properties, hydration behaviors, and environmental impact

Steel Slag/Precarbonated Steel Slag as a Partial Substitute for Portland Cement: Effect on the Mechanical Properties and Microstructure of Stabilized Soils

Influences of Ultrafine Slag Slurry Prepared by Wet Ball Milling on the Properties of Concrete

Effect of steel slag powder and stone powder by-product from manufactured sand on the mechanical properties and microstructure of cementitious materials

Influence of Ultra-Fine Slag and Silica Fume on Properties of High-Strength Concrete

Enhancement of ultra-fine slag on compressive strength of solid waste-based cementitious materials: Towards low carbon emissions

Sustainable Utilization of Waste Oyster Shell Powders with Different Fineness Levels in a Ternary Supplementary Cementitious Material System

Effects of Ultra-Fine Ground Granulated Blast-Furnace Slag on Initial Setting Time, Fluidity and Rheological Properties of Cement Pastes

Compressive-Tensile Mechanics and Energy Consumptions of a Cementitious Composite with High Utilization of Steel Slag

Effects of Steel Slag Powder as A Cementitious Material on Compressive Strength of Cement-Based Composite

Feasibility of Preparing Steel Slag–Ground Granulated Blast Furnace Slag Cementitious Materials: Synergistic Hydration, Fresh, and Hardened Properties