Electronic Structure and Magnetic Configuration of Ni-Substituted MnCo2O4 Spinel

Hongru Wang,Congmian Zhen,Jingtong Xie,Lu Liu,Li Ma,Dewei Zhao,Denglu Hou

DOI: https://doi.org/10.1021/acs.jpcc.0c07165

2020-01-01

Abstract:The electrical and magnetic structures of Ni-substituted MnCo2O4 have been studied theoretically and experimentally. With the increase of Ni concentration x, the calculated results show that the bond lengths of the Mn-O and Ni-O bonds along three directions (a, b, and c axis) tend to be consistent, and the lattice symmetry of NixMn1-xCo2O4 changes from tetragonal to cubic symmetry. The inverse spinel NixMn1-xCo2O4 was found to have a ferrimagnetic half-metallic ground state. The Ni dopant results in the flow of holes from the e(g,beta)(1 )level of Ni3+ at the octahedral site to the e(g,beta)(2 )level of Co2+ at the tetrahedral site. Therefore, the calculated conductivity type of NixMn1-xCo2O4 changes from n- to p- type as the Ni concentration increases. Furthermore, Ni3+ ion substitution in the MnCo2O4 spinel changed the relative position of the e(g,beta)(1 )level of Ni3+ at the octahedral site the e(g,beta)(2 )level of Co2+- at the tetrahedral site, which makes the activation energy E-A of NixMn1-xCo2O4 obtained from our experimental results decrease first and then increases with the x value increasing. Among all the doped samples, the Ni0.25Mn0.75Co2O4 has the smallest activation energy and the highest electrical conductivity. The measured room-temperature resistivity of the system is reduced by 5 orders of magnitude due to Ni doping.