Huajing Zhang,Chao Xu,Jiaxin Xing,Bowen Xu,Xiangyu Sun,Zhirong Liao,Xin Xia,Fei Jin
DOI: https://doi.org/10.1016/j.solmat.2023.112680
IF: 6.9
2023-12-24
Solar Energy Materials and Solar Cells
Abstract:The CaCO 3 /CaO materials are promising materials for thermochemical energy storage . However, they suffer from rapidly decreasing energy storage density over multiple calcination/carbonation cycles. This paper aims to select suitable inert supports with cyclic stability enhancement for the calcium looping (CaL) process at high carbonation reaction temperatures (>800 °C). Firstly, four metallic elements (Zr, Mn, Y and Ce) were selected, and a single-doping strategy was used to screen out single-doping inert supports. By comparison, the 20Ca–Zr had the best energy storage performance, with an energy storage density ( Eg,N=30 ) of 1744.72 kJ/kg after 30 cycles. Subsequently, the co-doping method was applied to further screen out co-doped combinations with long-term cyclic stability potential. The Zr was co-doped with Mn, Y and Ce, respectively. Among them, the 20Ca-0.5Zr-0.5Y displayed the best cyclic stability with an average energy storage density ( Eg,av ) of 1950.69 kJ/kg in 30 cycles. Based on the chosen Zr–Y co-doped CaO-based composite, the doping concentration optimization and multiple cycles tests were carried out. The effective conversion ( Xeff ) of 10Ca-0.5Zr-0.5Y decreased by only 4.9 % after 60 cycles. Therefore, the Zr–Y co-doped CaO-based composite, possessing robust sintering resistance effects, is promising for long-term TCES technology.
materials science, multidisciplinary,physics, applied,energy & fuels