Bifunctional Porous Organic Polymers Based on Postfunctionalization of the Ketone-Based Polymers

Lizhi Wang,Gui Chen,Qin Xiao,Du Zhang,Yafei Sang,Jianhan Huang

DOI: https://doi.org/10.1021/acs.iecr.0c04399

2020-01-01

Industrial & Engineering Chemistry Research

Abstract:Multifunctional porous organic polymers (POPs) are excellent porous materials for CO2 capture and Hg2+ adsorption. Especially, plentiful ultramicropores (d < 0.7 nm) and a high nitrogen (N) content are beneficial for CO2 capture, and the micropores and the specific functional groups are helpful for Hg2+ adsorption, while the facile construction of the multifunctional POPs still remains a challenge. Herein, a series of bifunctional POPs was simply fabricated from the ketone-based polymers on the basis of the postfunctionalization. Because of their low Brunauer-Emmett-Teller (BET) surface area (S-BET) and pore volume (V-total), the polymers were further carried out the Schiff-based reaction using melamine (MA) as the postmodifier. As the rigid external cross-linker, MA embedded in the pores of the polymers and supported the skeleton of the polymers. The resulting polymers showed a sharp increase of the S-BET (up to 703 m(2)/g) and V-total (up to 0.657 cm(3)/g), high N content (up to 36.95 wt %), and three-dimensional hierarchical porosity. In particular, the high ultramicropore volume (up to 0.199 cm(3)/g) of the resulting polymers made them effective for CO2 capture (193 mg/g; 273 K and 1 bar). The high micropore volume (up to 0.272 cm(3)/g) and abundant N (up to 36.95 wt %) offered them high Hg2+ capacity (425 mg/g at 298 K). This facile postfunctionalization strategy is potentially useful for the fabrication of some other multifunctional POPs.