Abstract:The (1 − x)(Li 0.03 Na 0.5 K 0.47 )(Nb 0.92 Sb 0.05 Ta 0.03 )O 3 –xBa 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (LNKNST–BCZT, x = 0, 0.5, 1.5, 2.5, and 3.5%) lead-free piezoceramics were synthesized by the conventional solid-state reaction method with adding nano-sized Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (BCZT) powder to investigate their influences on crystal structure and electrical properties. The X-ray diffraction (XRD) analysis reveals that all the sintered LNKNST–BCZT ceramics exhibit pure perovskite structure with the mainly rhombohedral (R) phase or the coexistence of rhombohedral (R) phase and tetragonal (T) phase. The composition of the LNKNST–1.5%BCZT ceramics locates around the critical point, i.e., the ceramics changing from the coexistence of rhombohedral (R) phase and tetragonal (T) phase to purely rhombohedral (R) phase, and presents the most densified microstructure morphology, which can be confirmed further by the field emission scanning electron microscope (FESEM) observation. There are two dielectric anomalies in the temperature dependent dielectric properties curves of the LNKNST–BCZT ceramics, which correlate with the ferroelectric rhombohedral (R) phase changing to the ferroelectric tetragonal (T) phase, and then to the paraelectric cubic (C) phase. Both the Curie–Weiss law and the power law fittings confirm the diffuse phase transition ferroelectrics characteristic of the LNKNST–1.5%BCZT ceramics, which is considered as correlating with the polar nanoregions (PNRs). Due to the densification effect caused by the chosen amount of nano-sized BCZT doping and the construction of R–T polymorphic phase boundary, the LNKNST–1.5%BCZT ceramics exhibit the best ferroelectric and piezoelectric properties. The complex impedance spectroscopy analysis confirms that the extrinsic electrical conduction mechanism at high temperatures is dominated by the oxygen vacancies induced by the evaporation of the alkali metals during sintering.

Effects of CuO on KNN-based Ceramics

Effects of Na Excess on the Preparation and Characterization of (K0.5na0.5)nbo3ceramics

Effect of CaZrO3 on phase structure and electrical properties of KNN-based lead-free ceramics

Effect of Microwave Sintering on KNN-based Lead Free Ceramics

Low-temperature Sintering of KNN-based Lead Free Ceramics

Effect of Three Step Sintering on Piezoelectric Properties of KNN-based Lead Free Ceramics

New Insight on Sintering Progress of KNN-Based Lead-Free Ceramics

Effects of CuO Doping on Properties of KNN-LS-BF Lead-free Piezoelectric Ceramics

(Bi0.5na0.5)(zr0.97w0.01fe0.02)o3 Doping Effects on KNN‐based Lead‐free Ceramics Prepared Via Two‐step Sintering Technique

Effects of nano-sized BCZT on structure and electrical properties of KNN-based lead-free piezoceramics

Effect of Shifting Orthorhombic-Tetragonal Phase Transition on Structure and Properties of K 0.5 Na 0.5 NbO 3 -Based Lead Free Ceramics

Microstructure and Piezoelectric Properties of CuO-doped 0.95(k0.5na0.5)nbo3–0.05li(nb0.5sb0.5)o3 Lead-Free Ceramics

Effect of Orthorhombic-Tetragonal Phase Transition on Structure and Piezoelectric Properties of KNN-based Lead-Free Ceramics.

The phase structure and electric properties of low-temperature sintered (K, Na)NbO3-based piezoceramics modified by CuO

Preparation of KNN Based Lead-Free Piezoelectric Ceramics Via Composition Designing and Two-Step Sintering

The Effect of Adding CuO on the Structure and Properties of NKN-based Lead-Free Piezoceramics

Effect of Sintering Time on Structure and Properties in CuO-doping KNN-LS-BF Piezoelectric Ceramics

Effects of Sintering Time on Properties of KNN-LS-BF-0.15％Cu Piezoelectric Ceramics

Effects of Sintering Temperature on Dielectric and Piezoelectric Properties of KNN-LS-BF-0.4mol%CuO Lead-Free Piezoelectric Ceramics

Effects of CuO on the Electrical Properties of CaTiO3‐Modified [(na0.52k0.48)0.955li0.045](nb0.955sb0.045)o3 Lead‐Free Piezoceramics

Influence on Structure and Properties of CuO Addition to KNN–LS–BF Piezoelectric Ceramics