Abstract:The microstructure, stress rupture properties and deformation mechanisms of a new alloy during long-term aging were investigated. The microstructure evolution mainly included the coarsening of gamma' phase and the precipitation of eta phase. During aging at 700 degrees C, 750 degrees C and 800 degrees C, the coarsening rate k of gamma' phase was about 7.818 nm(3)/h, 42.927 nm(3)/h and 178.226 nm(3)/h, respectively. The activation energy Q for gamma' coarsening was about 279.98 kJ/mol, which meant that element diffusion controlled the coarsening of gamma' phase. After aging at 750 degrees C for 3000 h and 800 degrees C for 2000 h, a new needle-like eta phase was precipitated near GBs and around MC carbides, then grew into the grain interiors. The quantity of eta phase increased with the increase of aging time. With the growth of eta phase, gamma' depleted zones were found around eta phase. This was principally because both gamma' phase and eta phase were enriched in Ni and Ti, and the growing up of I phase absorbed gamma' phase. After aging at 700 degrees C for 300-3000 h and 750 degrees C for 300-2000 h, the stress rupture life at 750 degrees C/430 MPa remained at a high level and most of them were higher than 100 h. That was because the slightly grown-up gamma' phase acted as strong obstacles to the dislocation motion, Orowan bypassing combing stacking fault shearing acted as the dominant mechanism during stress rupture deformation. After aging at 750 degrees C and 800 degrees C for 3000 h, the stress rupture life decreased to 45.7 h and 7.68 h, respectively. One reason was that the seriously grown-up gamma' phase was very hard to impede the dislocation motion, almost all gamma' phases were cut by dislocations with leaving stacking faults inside them during stress rupture deformation. The other reason was that needle-like eta phase promoted dislocation pile-up and contributed to the nucleation of micro-cracks, meanwhile the gamma' depleted zones could be conductive to the propagation of micro-cracks.

Microstructure Evolution and Stress Rupture Properties of K4750 Alloys with Various B Contents During Long-Term Aging

Effect of Boron Addition on the Microstructure and Mechanical Properties of K4750 Nickel-Based Superalloy

Effect of Grain Boundary Precipitates on the Stress Rupture Properties of K4750 Alloy after Long-Term Aging at 750 °C for 8000 H

Effect of Trace Boron Addition on the Microstructural Evolution and Mechanical Properties in Ti45al8nb2cr-B Alloys

Effect of Co on Microstructure and Stress Rupture Properties of K4750 Alloy

Precipitation of Η Phase and Its Effects on Stress Rupture Properties of K4750 Alloy

Effects of B content on microstructure and high-temperature stress rupture properties of a high chromium polycrystalline nickel-based superalloy

Effects of Microstructure Evolution on the Deformation Mechanisms and Tensile Properties of a New Ni-base Superalloy During Aging at 800 °C

Effect of Hafnium Content on the Microstructural Evolution and Stress Rupture Properties of K4750 Nickel-Based Superalloy

Precipitates Evolution During Isothermal Aging and Its Effect on Tensile Properties for an AFA Alloy Containing W and B Elements

Stress Rupture Properties and Deformation Mechanisms of K4750 Alloy at the Range of 650 °C to 800 °C

Formation and Kinds of Boride on Microstructure Evolution and Mechanical Properties in Ti47.5Al2.0Cr2.0NbxB Alloys

Effect of Initial Microstructure on the Properties of K439B Nickel-Based Superalloy During Prolonged Aging at 800 °C

Effect of Boron Microalloying on Microstructure and Thermoelastic Martensitic Transformation in Aged NiFeGa(B) Alloys

Microstructure and Crystallography of Borides and Mechanical Properties of Fe–B–C–Cr–Al Alloys

Effect of Long-Term Aging on the Microstructure, Stress Rupture Properties and Deformation Mechanisms of a New Cast Nickel Base Superalloy

Effect of Pouring System on Microstructure and Properties of K4750 Alloy

Effects of Boron on Microstructure Evolution and Mechanical Properties in Ti46Al8Nb2.6C0.8Ta Alloys

Effects of boron on the mechanical behaviour of a Ni-rich NiAl alloy

Effects of Carbon and Boron Addition on Microstructure and Mechanical Properties of TiAl Alloys

Effects of Aging Treatment on Microstructure and Impact Toughness of HR3C Alloy