Abstract:BACKGROUND For improving the permeability and selectivity of adsorption separation membranes, membrane materials, structural morphology and separation technology must continue to be investigated. Development of a membrane that is environmentally friendly, cost-effective and with high filter precision is an important direction in current research. RESULTS The air pressure spraying method was used to prepare an activated carbon (AC)-cellulose acetate/chitosan (CA/CS) composite membrane. The CA/CS fiber composite membrane was prepared as substrate layer, and AC was loaded on the surface of the CA/CS composite membrane as a functional adsorption layer. When the spraying pressure was 0.01 MPa and the mass ratio of AC/CS was 2:1, a composite membrane with even and compact morphology could be obtained. Both the compact AC functional layer and complete CA/CS substrate layer endowed the AC-CA/CS composite membrane with an excellent water filtration property. At low feeding pressure, the permeate flux and rejection rate of bisphenol A (BPA) could reach 9.27 x 10(3)L m(-2)h(-1)and 98.31%, respectively. Meanwhile, the adsorption capacities of the membrane were investigated. It tended to equilibrate quickly in 2 min for dyes and BPA. The equilibrium adsorption capacities of the membrane for acid blue, acid yellow and BPA were 175.80, 164.0815 and 79.58 mg g(-1), respectively. The adsorption process conformed to pseudo-second-order kinetics and the Langmuir monolayer adsorption model. CONCLUSIONS This work could provide a practical and effective feasibility for membrane separation technology. (c) 2020 Society of Chemical Industry (SCI)

Highly Efficient Separation Membrane Based on Cellulose Acetate/chitosan Fibrous Composite Substrate with Activated Carbon Functional Adsorption Layer