Study on formability and deformation behavior of friction stir welding AA2024-7075 joint
Wenbin Xu,Jiaheng Zhang,Qiu Pang,Zhi-li Hu
DOI: https://doi.org/10.1007/s00170-023-12081-x
IF: 3.563
2023-08-10
The International Journal of Advanced Manufacturing Technology
Abstract:Aluminum alloy tailor-welded blank (TWB) forming can achieve both material lightweight and structural lightweight, especially that dissimilar aluminum alloy TWB forming can better adapt to the different performance requirements of different parts of aerospace and automotive lightweight components to further achieve weight reduction and has a wide range of engineering application prospects. In this work, 2024-O and 7075-O aluminum alloy are used as the object of study. By observing the microstructure and measuring mechanical properties, establish the multiple- materials strength-mismatched of dissimilar friction stir welding (FSW) AA2024-7075 joints, to research the formability and deformation behavior of dissimilar FSW AA2024-7075 joints under different strength-mismatched conditions. Results show that during the tensile deformation of the dissimilar FSW AA2024-7075 joint, the equivalent stresses and strains in the weld nucleus area (WNZ) experience several abrupt changes. In the mixed WNZ of microstructures of the 2024WNZ and 7075WNZ, the AA7075 with high yield strength will have a restraining and protective effect on the AA2024 with low yield strength, which suppresses the deformation of AA2024. The heterogeneous microstructure of the dissimilar FSW AA2024-7075 joint leads to severe inhomogeneous deformation, which reduces the elongation. The 350 ℃ annealing heat treatment effectively reduces the inhomogeneity of the microstructure of each zone, lowers the difference of mechanical properties between AA2024 and AA7075, improves the uniformity of deformation of the dissimilar FSW AA2024-7075 joint, and increases the elongation from 8.5% to 12.8%.
engineering, manufacturing,automation & control systems