Immobilizing Chromium in Stainless Steel Slags with MnO Addition

Zhanjun Wang,Il Sohn
DOI: https://doi.org/10.1111/jace.17473
IF: 4.186
2020-01-01
Journal of the American Ceramic Society
Abstract:This work investigates the stabilizing impact of MnO on the leaching behavior of hazardous Cr-containing CaO-SiO2-Al2O3-Cr2O3-MnO stainless steel slags after equilibrating at various elevated temperatures and evaluates the potential immobilization of Cr into a MnCr(2)O(4)spinel phase from the existing Cr(2)O(3)phase. The MnCr(2)O(4)spinel phase was found to be an excellent Cr-stabilizer in stainless steel slags, where the leaching tendency of potentially hazardous Cr-related ions decreased with higher MnO content and lower equilibration temperatures within the range of 0 to 15 mass pct. and 1500 to 1300 degrees C, respectively. Thermodynamic calculations by conducting the phase stability diagram also showed that the MnCr(2)O(4)spinel phase was relatively stable and the Ca3Si2O7(Ca3-xMnxSi2O7) phase was relatively unstable compared with other crystal phases in acid extractant with pH value of 3.2. Combined with the scanning electron microscopy and X-ray powder diffraction results along with the thermodynamic calculations, the leached Cr-related ions was predominantly originating from the unstable amorphous glass phase.
What problem does this paper attempt to address?