Facile fabrication of fibrous Bi 4 Ti 3 O 12 /Bi 2 S 3 /MoS 2 with enhanced photocatalytic activities towards pollutant degradation under visible light irradiation

Jun Liu,Qian Hui,Meng-Jie Chang,Wen-Na Cui,Tong Xi,Lin-Da Wang,Meng Sun,Bin Yuan,Fu-Rong Ni
DOI: https://doi.org/10.1007/s10854-020-04324-4
2020-01-01
Abstract:Herein, novel fibrous Bi 4 Ti 3 O 12 /Bi 2 S 3 /MoS 2 is constructed by a simple one-step methodology for photocatalytic degradation of RhB dyes. Bi 4 Ti 3 O 12 /Bi 2 S 3 /MoS 2 hybrid fibers were facilely prepared by direct hydrothermal growth of MoS 2 nanosheets on electrospun Bi 4 Ti 3 O 12 nanofiber surface, during which rod-like Bi 2 S 3 was formed by in-situ ion exchange reaction between BTO and S source. The MoS 2 nanosheets with several-layer thickness uniformly are coated both on the BTO and Bi 2 S 3 surface. Remarkable enhancement of visible light absorption and photo-generated charge separation in Bi 4 Ti 3 O 12 /Bi 2 S 3 /MoS 2 are achieved compared with the bare BTO nanofibers. By changing the weight ratio of Mo/S and the precursor dosage of MoS 2 , the optimized BM-150/250 sample presents 2.3 and 4.1 times higher of the photodegradation efficiency and apparent reaction rate constant, respectively, than that of pure BTO fibers after 120-min irradiation under visible light. The system pays an efficient pathway to establish ternary composite fibers providing high photocatalytic activity for other electrospun Bi-contained nanofibers.
What problem does this paper attempt to address?