Aliovalent Doping Engineering for A- and B-Sites with Multiple Regulatory Mechanisms: A Strategy to Improve Energy Storage Properties of Sr 0.7 Bi 0.2 TiO 3 -Based Lead-Free Relaxor Ferroelectric Ceramics
Peng Zhao,Zixuan Fang,Xingchen Zhang,Jingjing Chen,Yidi Shen,Xing Zhang,Qi An,Chengtao Yang,Xingsen Gao,Shuren Zhang,Bin Tang
DOI: https://doi.org/10.1021/acsami.1c04274
2021-05-20
Abstract:Sr<sub>0.7</sub>Bi<sub>0.2</sub>TiO<sub>3</sub> (SBT) is a promising pulse energy storage material due to minor hysteresis, but its low maximum polarization (<i>P</i><sub>max</sub>) is bad for energy storage. K<sup>+</sup>–Bi<sup>3+</sup> defect pairs were introduced into the A-site of SBT to obtain Sr<sub>0.35</sub>Bi<sub>0.35</sub>K<sub>0.25</sub>TiO<sub>3</sub> (SBKT) with larger <i>P</i><sub>max</sub>. Through first-principles calculations, we determined that the introduction of defect pairs destroys the paraelectric order phase and increases local polarization, resulting in more and larger polar nanoregion (PNR) formation. On this basis, doping NaNbO<sub>3</sub> (NN) in A- and B-sites of SBKT increases the cationic disorder and ferroelectric destabilization, further destroying the long-range order structure and forming more PNRs with smaller sizes. This enhances relaxation and decreases remnant polarization, and the broadened dielectric peak enables 0.85SBKT–0.15NN to meet the X7R specification. Furthermore, the decreased grain size and oxygen vacancy, increased thermal conductivity, and weakened local electric field (simulated by COMSOL) increase the dielectric breakdown strength (BDS). As a result, 0.95SBKT–0.05NN exhibits a high energy storage density (<i>W</i>) of 2.45 J/cm<sup>3</sup> with a high efficiency of 93.1%, a high pulsed discharge energy density of 2.1 J/cm<sup>3</sup>, and a high power density of 54.1 MW/cm<sup>3</sup> at 220 kV/cm. The energy storage properties show excellent stability of temperature (−55 to 150 °C), frequency (10–500 Hz), and cycling (10<sup>5</sup> cycles). Notably, for the pulse charge–discharge properties, 0.95SBKT–0.05NN shows great fatigue resistance during 10<sup>5</sup> cycles under 25 and 150 °C, accompanied by excellent thermal stability. Moreover, the BDS and <i>P</i><sub>max</sub> of 0.95SBKT–0.05NN sintered in O<sub>2</sub> further enhance. A higher <i>W</i> of 2.92 J/cm<sup>3</sup> with a high efficiency of 89% at 250 kV/cm is achieved. Therefore, 0.95SBKT–0.05NN shows great application potential for pulse energy storage. In this work, we provide a novel strategy and systematic in-depth study for improving the energy storage properties of SBT.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c04274?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c04274</a>.Details of simulation and calculation methods; refined XRD data; TEM images of the second phase of SBKT; formation mechanism of Na<sup>+</sup>–Bi<sup>3+</sup> defect polar pairs; EDS test results of 0.95SBKT–0.05NN; temperature dependence of dielectric constant and loss for SBKT–NN ceramics; plots of 1/ε<sub>r</sub> as a function of temperature and <i>T</i><sub>m</sub> and <i>T</i><sub>B</sub> of SBKT–NN ceramics; topography images and amplitudes images with written domain patterns; phase hysteresis loops and butterfly amplitude loops measured at the local position of SBT; Vogel–Fulcher fit of SBKT–NN ceramics; ε<sub>r</sub> of SBKT–NN under different biases; Weibull distribution of BDS; numerical simulation results (situation I); Arrhenius-type plots of DC electrical conductivity and characteristic frequency of SBKT–NN ceramics; calculation method of <i>E</i><sub>f</sub>, <i>E</i><sub>f</sub>, and leakage current density of SBKT–NN ceramics; energy storage properties of SBKT–NN ceramics; <i>P</i><sub>max</sub> and <i>P</i><sub>r</sub> under critical electric fields of SBKT–NN ceramics; <i>P</i>–<i>E</i> loops, <i>J</i>–<i>E</i> loops, and energy storage properties under different electric fields of 0.95SBKT–0.05NN ceramics; <i>P</i><sub>max</sub> and <i>P</i><sub>r</sub> of stability test of 0.95SBKT–0.05NN ceramics; <i>W</i><sub>d</sub>, <i>t</i><sub>0.9</sub>, and <i>T</i> values of 0.95SBKT–0.05NN ceramics; discharge current of overdamped current–time curves under different temperatures of 0.95SBKT–0.05NN ceramics; <i>W</i><sub>d</sub>, <i>t</i><sub>0.9</sub>, discharge current, underdamped current–time curves, and <i>P</i><sub>D</sub> with 10<sup>5</sup> cycles for 0.95SBKT–0.05NN ceramics; SEM image, XRD patterns, Weibull distribution of BDS, XPS of spectra the O 1s valance state, and Arrhenius-type plots of DC electrical conductivity of 0.95SBKT–0.05NN ceramics sintered in O<sub>2</sub>; calculation method of ε<sub>r</sub>; and table and literature of comparison of charge–discharge performance and energy storage properties (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c04274/suppl_file/am1c04274_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology