In Situ Investigation of the Deformation Behaviors of Fe20Co30Cr25Ni25 and Fe20Co30Cr30Ni20 High Entropy Alloys by High-Energy X-ray Diffraction

Ning Xu,Shilei Li,Runguang Li,Minghe Zhang,Zhiran Yan,Yuxian Cao,Zhihua Nie,Yang Ren,Yan-Dong Wang
DOI: https://doi.org/10.1016/j.msea.2020.139936
2020-01-01
Abstract:In situ synchrotron-based high-energy X-ray diffraction (HE-XRD) technique was employed to investigate the mechanical behaviors and microstructural evolution of face-centered cubic (FCC) Fe20Co30Cr25Ni25 and Fe20Co30Cr30Ni20 high entropy alloys (HEAs) during tensile deformation. Fe20Co30Cr30Ni20 HEA has a good combination of strength (ultimate tensile strength of 864 +/- 35 MPa) and ductility (elongation of 0.627 +/- 0.021). The HE-XRD investigation reveals that Fe20Co30Cr30Ni20 HEA has the transformation-induced plasticity (TRIP) effect, which starts at a critical stress of similar to 555 MPa. Transmission electron microscopy confirmed this deformation-induced new phase is hexagonal-close-packed structured c-martensite, which follows an orientation relationship of {111}(gamma)/(0001)(epsilon), and < 110 >//[11 (2) over bar0](epsilon) with the FCC gamma matrix. The observation of deformation twins in the deformed samples of the two studied HEAs proves that twinning-induced plasticity (TWIP) effect occurs in both HEAs. The combination of TRIP and TWIP effects lead to the high strength, large ductility and improved strain hardening behavior of Fe20Co30Cr30Ni20 HEA.
What problem does this paper attempt to address?