Two Anionic Ni(II) Porphyrinic Metal−organic Frameworks: Syntheses, Flexibility and Roles in Visible-Light Photocatalytic CO2 Reduction to CO in the Ru(bpy)3Cl2/TEA/CH3CN System

Tao Chen,Jie Ding,Tianyu Liu,Qi Li,Yanping Luo,Longzhang Dong,Hongbin Du,Min Fang,Jianchun Bao,Yong Wu
DOI: https://doi.org/10.1016/j.jssc.2020.121340
IF: 3.3
2020-01-01
Journal of Solid State Chemistry
Abstract:A 3D, anionic novel porphyrinic metal-organic framework (PMOF) 1 having [NH2(CH3)(2)](+) as counterions and Li+-exchanged version of 1 (Li+-1) were synthesized. A very interesting feature of 1 and Li+-1 is their frameworks can change shape without breaking bonds, causing substantial changes of their PXRD patterns depending on what and how much is in the channels. Li+-1 has much larger surface area (Langmuir: 640 m(2)/g), compared with the 339 m(2)/g of PMOF 1. The CO2 adsorption capacities of 1 and Li+-1 are 38 (7.5 wt%) and 45 mL/g (8.9 wt%), respectively at 1 atm and 298 K, and 165-167 mL/g (33%) at 9.9 atm. They are direct-bandgap semiconductors with bandgaps of 1.56 (for 1) and 1.62 (for Li+-1) eV. The conduction and valence band-edge positions were determined in non-aqueous solutions as -0.29 and 1.27 (1), -0.32 and 1.30 V (Li+-1) versus NHE. PMOF 1 or Li+-1/Ru(bpy)(3)Cl-2/TEA/CH3CN (bpy = 2,2-bipyridine, TEA = triethylamine) system photocatalytically reduce CO2 to CO under visible light. PMOFs act as cocatalysts, and the photocatalysts were found to be the triplet excited state of Ru(bpy)i+ (Ru(II)*) and its photodecomposition products. The TOFs contributed from PMOFs after 2 h were 0.091 and 0.097 h(-1) (224 and 241 mu mol g-h(-1)), respectively for 1 and Li+-1, respectively. In addition, the Ru(bpy)(3)Cl-2/TEA/CH3CN system were found to have an unprecedented high TOF of 0.31 h(-1) (412 mu mol g-h(-1)) when small amounts of H2O (200 uL H2O in 40 mL CH3CN and 10 mL TEA) was added.
What problem does this paper attempt to address?