Incorporation of Light-Emitting Polymer into Large Cage-Type Mesoporous Silica: Toward New Luminescent Nanocomposites
Zhang Wenkai,Hu Chenglong,Huang Yunyun,Zhang Mingqiu,Liang Hui,Chen Xudong
DOI: https://doi.org/10.6023/a12090679
2012-01-01
Acta Chimica Sinica
Abstract:Light-emitting conjugated polymers confined in mesoporous environment create an opportunity for control of the polymer morphology for design of new functional composite materials with suitable qualities. A novel polyfluorene derivative, poly[N-octylcarbazole-co-9,9'-dioctylfluorene-co-1,3,4-oxadiazole] (PCFOz) was synthesized via Pd-catalyzed Sonogashira reaction in a mixture of 3,6-dibromo-9-octylcarbazole, 2,5-bis-(4-bromo-phenyl)-[1,3,4]-oxadiazole and 2,7-diethyne-9,9'-dioctylfluorene with Pd(PPh3)(2)Cl-2 and CuI as the catalyst. The large cage-like mesoporous silica FDU-12 with hexagonal prism morphology was successfully synthesized and modified with TMCS (trimethylchlorosilane). The composite material was prepared by incorporating PCFOz into FDU-12 via one-step liquid-phase self-assembly method, and then fully characterized by mean of X-ray diffraction, nitrogen physisorption porosimetry, scanning electron microscopy (SEM), transmission electron microscope (TEM) and thermogravimetric analysis. The absorption spectra of composites showed a red-shift-and narrower band as compared to pristine film, indicating the polymer chains packing in a special style in the cage type pores with a narrower excitonic energy distribution. PL spectra of composite materials suggested that the cages could incorporate more than one chain but less interchain species formed in cages compared with aggregates in film. The fluorescence decay kinetics observed longer exciton lifetimes in the composites resulting from the reduced exciton mobility and strong torsional distortions. Fluorescence signal from composite materials observed by laser scanning confocal microscope showed 20-times-higher than that obtained from pristine polymer film. Temperature dependence of PL spectra of composites was examined by heating the samples from 40 to 450 K, resulting in less than 10% decrease of PL intensity but no spectra variation for nanocomposites, as compared with 52% decrease of PL intensity accompanying with green-band rising for pristine PCFOz. Photostability tests were performed under the radiation of highly focused UV beams, suggesting that the excitons in the PCFOz within the pores of FDU-12 possessed better environmental stability.