High-Performance Supercapacitors Based on Hierarchical VOx Microspheres Forming from Hyperbranched Nanoribbons

Chuang Wei,Hong-Yi Li,Zhao Yang,Bing Xie
DOI: https://doi.org/10.1007/978-3-319-51493-2_1
2017-01-01
Abstract:Novel VOx nanomaterials as high performance electrode materials of supercapacitors were successfully synthesized by solvothermal method using V2O5, H2O2, (NH4)(2)SO4 and EG (Ethylene Glycol). These as-prepared nanomaterials are hierarchical microspheres with diameter of similar to 5 mu m, which formed from hyper-branched growth of nanoribbons. According to XRD and TEM, these hierarchical VOx microspheres consist of V6O13 with metallic conductivity and VO2. These materials exhibited a tremendous specific capacitance of 581 F/g, with corresponding volumetric specific capacitance of 3.94 F/cm(3), at 0.6 A/g in the potential range of 0 to 1.2 V when used as supercapacitor electrodes in a solution of 1 M LiNO3. The energy density is as high as 29 Wh/kg, which is much higher than those of many other symmetrical supercapacitors. In addition, the capacity retention of 65% was achieved even after 2000 cycles, demonstrating high performance of vanadium oxide nanomaterials used in supercapacitors.
What problem does this paper attempt to address?