Biosynthesis of Magnesium Phosphates and Its Thermal Property

Xiaoniu Yu,Chunxiang Qian,Xin Wang

DOI: https://doi.org/10.1166/sam.2015.2392

2015-01-01

Science of Advanced Materials

Abstract:Bacillus subtilis was selected to investigate microbe induced magnesium phosphates precipitation. Structure and morphology of magnesium phosphates were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Characterized results show that nanostructures of magnesium phosphates were prepared by biological deposition. SEM images show that the mixture of MgHPO4 . 1.2H(2)O and Mg-3(PO4)(2) 5H(2)O, and Mg-3(PO4)(2) 5H(2)O are nano-clusters and honeycomb in shape respectively, with size in the range of 1-3 mu m. TEM photographs further display that the mixture is amorphous morphology and no ED patterns, and the Mg-3(PO4)(2)5H(2)O is yet nano-sheet in shape with size in the range of 50-100 nm and have a good ED patterns. And thermal properties of magnesium phosphates were investigated via thermogravimetric-differential scanning calorimetry (TG-DSC) analysis. The mixture of MgHPO4. 1.2H(2)O and Mg-3(PO4)(2).5H(2)O of weight-loss was about 45.03% which was caused by the elimination of crystal water and decomposition of MgHPO4. Mg3(PO4)2, which was produced by Mg-3(PO4)(2.).5H(2)O losing crystal water, of crystallization temperature was 698.7 degrees C, resulting in total weight-loss of 32.55%.