Synthesis and Photoluminescence Properties of Eu3+-Doped Na2YMg2V3O12: A Novel Red-Emitting Phosphor for White-Light-Emitting Diodes
Weiyi Zhang,Yanqiu Shao,Ying Zhu,Yingying Shao,Zhaohui Huang,Min Xin,Yangai Liu,Can He,Xiaoguang Zhang
DOI: https://doi.org/10.21203/rs.3.rs-736843/v1
2021-07-27
Abstract:Abstract The fabrication and luminescent properties of novel Na 2 YMg 2 V 3 O 12 :Eu 3+ phosphors produced by conventional solid-state reactions were investigated. Self-activated emission of the Na 2 YMg 2 V 3 O 12 host produces a broad emission band ranging from 400 to 700 nm with a maximum peak at 530 nm, ascribed to the charge transfer in the (VO 4 ) 3− groups. Excitation with near-UV (365 nm) light causes the Na 2 YMg 2 V 3 O 12 :Eu 3+ phosphors to emit bright red light, including both the broad emission band of the (VO 4 ) 3− groups and the sharp emission peaks of Eu 3+ ions. At a quenching concentration of 0.03 mol, the Eu 3+ ion emission peaks were located at 597, 613, 654 and 710 nm. As-prepared Na 2 YMg 2 V 3 O 12 :Eu 3+ phosphors also exhibited stable emission at high temperatures. Furthermore, a designed and packaged white-light-emitting diode (WLED) lamp, including the obtained phosphors, commercial (Ba,Sr) 2 SiO 4 :Eu 2+ green phosphors, BaMgAl 10 O 17 :Eu 2+ blue phosphors and a near-ultraviolet (n-UV) chip, emitted bright white light with a good chromaticity coordinate of (0.3068, 0.3491), a satisfactory colour rendering index of 88.20 and a properly correlated colour temperature of 4460.52 K. These results indicate the potential of this Na 2 YMg 2 V 3 O 12 :Eu 3+ phosphor as a red-emitting phosphor for solid-state illumination.