Facile Synthesis of a Unique Interleaved Graphene-Embedded Sulfur Nanocomposite As Cathode of Li-S Batteries with Excellent Lithium Storage Performance
Yun-Xiao Wang,Ling Huang,Yue-Feng Xu,Jun-Tao Li,Shi-Gang Sun
DOI: https://doi.org/10.1149/ma2012-02/10/922
2012-01-01
ECS Meeting Abstracts
Abstract:Sulfur possesses almost the highest theoretical capacity of 1675 mA h g and the highest theoretical specific energy of 2600 Wh kg among all known conventional cathode materials. Along with the abundant resources, low equivalent weight, low cost and environmental friendliness, the sulfur has a significant potential to be used in next-generation batteries with high capacity and energy density. In spite of the exceptional valuable characteristics of Li-S battery, however, the sulfur cathode with an organic liquid electrolyte is facing on challenges including low utilization of active material and severe capacity fading, which are mainly ascribed to the insulating nature of sulfur and its final charge products, the solubility of the long chain polysulfide ions, and the deposition of insoluble Li2S2/Li2S on the cathode. To successfully operate a Li-S battery, various strategies were developed, mainly in exploration of electrode coatings, inorganic additives, conductive additives and multifunctional binders, as well as optimizing the organic electrolytes etc. Nevertheless,the most effective method is to enable the pure sulfur well dispersed into a conductive and strong adsorbent additive. Different kinds of carbonaceous materials have received much attention because of their structure, conductivity and good electrochemical stability. Remarkable progresses have been made recently. In these studies, sulfur was loaded into ordered mesoporous carbon materials, which ensured a more efficient electronic contact and a high content of sulfur in the composite. As a consequence, a higher volumetric energy density, a higher capacity and a better rate capability have been achieved. Currently, a new kind of carbon material, graphene, has triggered extensive interests. Graphene offers exceptional advantages owing to its high surface area, unique conductivity, ultrathin thickness, superior structural flexibility and good mechanical properties. More importantly, its nanostructures with significant disorders, expansion of interlayer spacing and numerous active defects make it the most attractive material as an efficient host of sulfur and a good electronic conductor of the sulfur cathode. In this paper, the graphene, which exhibits the advantages of high conductivity and large surface area was synthesized by modified Hummers’ method. The sulfur-graphene nanocomposite was prepared by simple melt-diffusion strategy. Superior lithium storage performances of the flexible interleaved nanocomposite of graphene-embedded sulfur (S-GNS) have been revealed. The study has thrown light on the particular crucial role of the graphene for maximum utilization of active sulfur. As shown clearly in Figure 1a, the XRD profile of graphene (black line) exhibits a broad weak (002) diffraction peak at 2θ of 26°, which can be assigned to disordered stacks of graphene nanosheets. In comparison with the pattern of 0.6S-GNS mixture ( containing 60% sulfur) before heating treatment (blue line), the XRD spectra of the 0.6S-GNS (red line) yields less peaks of smaller intensity, implying that sulfur is mainly anchored into the graphene framework and the excess sulfur becomes nanosized crystalline sulfur in the cooling process. Furthermore, the peak positions indicate that orthorhombic sulfur phase has been transformed into monoclinic sulfur in the preparation process. The morphology of 0.6S-GNS shown by SEM image in Figure 1b is similar to that of pure graphene, signifying that bulk crystalline sulfur completely disappear on the surface. Such result implies that a large amount of sulfur existing as small nanoparticles is completely loaded into interlayer spacing, edges and defects of the graphene nanosheets. The elemental mappings of sulfur and carbon of the area outlined by the red frame in Figure1c further corroborate that the sulfur is homogeneously embedded into the framework of graphene host, which is ascribed to the favourable fluidity of molten sulfur.