Synthesis and Degradation Behavior of Miktoarm Poly(ɛ-Caprolactone) 2 - B -Poly( L -Lactone) 2 Microspheres

Xi Zhang,Yan Xiao,Meidong Lang

DOI: https://doi.org/10.1038/pj.2012.166

IF: 3.135

2013-01-01

Polymer Journal

Abstract:Poly(ɛ-caprolactone) 2 - b -poly( L -lactide) 2 miktoarm block copolymers were successfully synthesized via ring-opening polymerization using pentaerythritol as the initiator and a protection–deprotection procedure. 1 H nuclear magnetic resonance ( 1 H NMR) and size exclusion chromatography (SEC) were employed to characterize the miktoarm structure, molecular weight and molecular weight distribution. The microspheres of poly(ɛ-caprolactone) 2 - b -poly( L -lactide) 2 ((PCL) 2 - b -(PLLA) 2 ) were produced by an oil-in-water emulsion solvent extraction/evaporation method and studied with scanning electron microscopy (SEM). The hydrolytic degradation of microspheres with different architectures and compositions was performed at 37 °C in a phosphate-buffered saline solution (pH=7.4). The weight loss of the microspheres was strongly affected by the molecular architecture, chain length and composition. The compositional, or molar ratio, changes were monitored during the degradation using 1 H NMR, SEC, differential scanning calorimetry and SEM, all of which suggested that the degradation proceeded from the surface to the interior and could be described using a combined degradation model with surface erosion and bulk degradation.