Phosphorus-based Triazine Compound Endowing Epoxy Thermosets with Excellent Flame Retardancy and Enhanced Mechanical Stiffness

Weiqi Xie,Shiwen Huang,Shumei Liu,Jianqing Zhao

DOI: https://doi.org/10.1016/j.polymdegradstab.2020.109293

IF: 5.204

2020-01-01

Polymer Degradation and Stability

Abstract:Searching highly-efficient flame retardants for flame-resistance and smoke-suppressed epoxy thermosets with enhanced mechanical performance has aroused considerable interest in the field of flame-retardant materials. Herein, a phosphorus-based flame retardant, 6,6',6 ''-(1,3,5-triazine-2,4,6-triyl)tris(oxy))tris(3-methoxybenzene-4,1-diyl))tris(hydroxymethylene))tris(dibenzo[c,e][1,2]oxaphosphinine 6-oxide) (Trif-D), was synthesized using a two-step method and served as the flame-retardant additive for commercial epoxy thermoset. The epoxy thermoset with the low loading of 5.0 wt% Trif-D (Trif-D-5, phosphorus content = 0.39 wt %) possessed a UL-94 V-0 rating (with a limiting oxygen index of 33.1%). According to the cone calorimeter test, compared with epoxy thermoset without Trif-D addition (Trif-D-0), the reductions of peak heat release rate and total smoke production in Trif-D-5 were 66.3% and 51.3%, respectively. The mechanism analysis confirmed that the phosphorus-based structure from Trif-D contributed both the gaseous-phase and condensed-phase flame retardance of epoxy network. Moreover, Trif-D-5 possessed the high mechanical stiffness due to the introduction of rigid structures (phosphaphenanthrene, triazine and benzene) from Trif-D, showing 5.2%, 3.6% and 5.9% increase in storage modulus (at 30 degrees C) (3.03 GPa vs. 2.88 GPa), tensile modulus (3.47 GPa vs. 3.35 GPa) and flexural modulus (2.89 GPa vs. 2.73 GPa) as compared to Trif-D-0, respectively. The present paper investigates a facile method for the fabrication of high-performance epoxy thermosets with excellent flame retardance and enhanced mechanical stiffness. (C) 2020 Elsevier Ltd. All rights reserved.