Enhanced energy density and efficiency of all-organic composites by designing multilayer gradient structure
Yuan Liu,Hang Luo,Fan Wang,Zhida Xiao,Chenchen Yang,Xiaona Li,Bo Peng,Yuting Wan,Jian Yin,Dou Zhang
DOI: https://doi.org/10.1039/d3tc01845h
IF: 6.4
2023-07-13
Journal of Materials Chemistry C
Abstract:Dielectric capacitors have bright application prospects in the field of pulse power devices due to their extremely high power density. However, a well-known challenge is how to achieve high discharge energy density and energy efficiency simultaneously. Herein, inspired by the multi-stage filtration mode of the water purifier, a new all-organic multilayer structured composite is designed to solve the dilemma, where gradient transition layers are designed, i.e. fluorene polyester (FPE) as the lower layer to maintain high breakdown strength, poly(vinylidene fluoride) (PVDF) as the upper layer to provide high dielectric constant, and composites layers consisting of different weight ratios of FPE and PVDF. The gradient transition layers play an important role in homogenizing the electric field and suppressing leakage current. As results, a discharge energy density as high as 12.70 J/cm3 and an energy efficiency up to 74.6% are achieved in the designed composite at 510 kV/mm, which is 2.3 times and 42.1% higher than that of FPE (3.83 J/cm3 at 450 kV/mm) and PVDF (52.5% of 420 kV/mm), respectively. The composites also exhibit excellent cycling stability and fast charge-discharge rate. For example, after 106 times charge discharge cycles at 200 kV/mm, the discharge energy density still hasn't decayed. In addition, the multilayer structured composite exhibits higher power density (5.77 MW/cm3) at 420 kV/mm than that of pure PVDF (3.57 MW/cm3) and FEP (3.38 MW/cm3). This work provides reliable experimental guidance for the development of all-organic dielectric capacitors with high performance.
materials science, multidisciplinary,physics, applied