GTA Weld Brazing a Joint of Aluminum to Stainless Steel

H. He,W. Gou,S. Lin,C. Yang,P. F. Mendez

DOI: https://doi.org/10.29391/2019.98.030

IF: 2.2

2019-01-01

Welding Journal

Abstract:The relationship between heat input, microstructures, and mechanical properties was studied in the gas tungsten arc (GTA) weld brazing process of aluminum alloy and stain-less steel dissimilar metals with a pure aluminum core wire (ER1100). The mechanisms involved were further revealed by hot-dip aluminizing experiments. The intermetallic compounds (IMCs) of the brazing interface consisted of a thin layer of -Fe2Al5 next to the steel, and a thick layer of -Fe4Al13 adjacent to the Al joint, surrounded by eutectic identified to be Al-FeAl6 and Al-Fe2Al9 distributed uniformly in the weld metal. With increasing heat input, the total thickness of the IMCs decreased first, reaching a minimum value of 3.5 m, and then increased. The decrease in IMC thickness with heat input was observed for the first time and had never been reported before in welding or brazing processes. The joint strength increased to a maximum value of 238 MPa and then declined, suggesting an inverse relationship between IMC thickness and joint strength. The results of the hot-dip aluminizing, regarding the relationship between IMC thickness and temperature, were consistent with the change of IMC thickness in the welds. A possible mechanism in action is that interfacial kinetics and thermodynamics play a role in the dissolution and decomposition of the thick layer of -Fe4Al13 into the FeAl6 and Fe2Al9 phase. Promoting the IMC dissolution or decomposition by adjusting welding procedures is a promising new way to control the IMC growth and improve the joint strength.