Effect Of Matrix Molecular Motion Ability On Positive Temperature Coefficient Behaviors Of Poly(Vinylidene Fluoride)/Carbon Fibers Composite
Ren-Peng Liu,Hui-Zhao Zou,Yan-Hao Huang,Zheng-Ying Liu,Wei Yang,Ming-Bo Yang
DOI: https://doi.org/10.11777/j.issn1000-3304.2020.20181
2021-01-01
Acta Polymerica Sinica
Abstract:Conductive polymer composites with positive temperature coefficient (PTC) effect have been widely utilized in electronic industry due to their low density, excellent processibility and abundant adjustability. At the melting temperature, the phase transition of crystalline region results in volume expansion, which leads to a dramatic increase in volume resistivity of the composite. Therefore, the PTC performances are highly correlated with the melting process and melt properties of polymer matrix, which means the motion ability of molecules chain during matrix melting affects the performances of the composite such as PTC intensity and reproducibility. Making a thorough inquiry of the effects of polymer molecular motility on PTC behavior is helpful for the design and fabrication of polymer based PTC materials with highly sensitive response to temperature and stable reproducibility in heating-cooling cycles. In this study, the resistance-temperature characteristic of carbon fibers (CF) filled poly(vinylidene fluoride) (PVDF) composites with varied melt viscosity of PVDF was investigated. All the samples showed significant PTC effect during heating processes without negative temperature coefficient (NTC) effect even at temperatures much higher than the melting point of polymer matrix. It can be found that the PTC transition temperature range depended only on the chemical structure and crystallinity of PVDF, while the cyclic stability of PTC behavior was significantly affected by the motion ability of the matrix molecules. For the PVDF(710)/CF composite with matrix of stronger molecular motion, during the heating cycles, the molecular chains possibly stuck to the fillers surface to form an insulating layer, which resulted in wider gaps between fillers and thus reduced tunneling current. After cooling, the reconstruction of conductive paths in composites was impeded, resulting in higher resistivity at room temperature, lower PTC intensity and worse reproducibility. On the contrary, in the PVDF(5130)/CF composites with higher matrix viscosity, the molecular chains with weaker motion ability would not cover CF particles. The composite could almost rebuild the conductive paths to the initial condition after heating-cooling cycles, thus stabilizing a better PTC reproducibility and stable resistivity at room temperature. When applied in the circuit overheat protection device, the PVDF(5130)/CF composite shut off the current timely at 167 degrees C and recovered the circuit when cooled down, exhibiting excellent sensitivity and reproducibility as thermal responsive switch.