Nanostructure evolution of silica aerogels under rapid heating from 600 C to 1300 C via in-situ TEM observation
Huafei Cai,Yonggang Jiang,Jian Feng,Qu Chen,Sizhao Zhang,Liangjun Li,Junzong Feng
DOI: https://doi.org/10.1016/j.ceramint.2020.02.011
IF: 5.532
2020-01-01
Ceramics International
Abstract:Silica aerogel is a typical nanoporous material exhibiting excellent thermal insulation property, and its nanostructure change at high temperature has attracted extensive attention. However, there is a lack of real-time research on the nanostructure evolution of silica aerogel under rapid heating. Here, silica aerogel was rapidly heated and imaged via an in-situ heating TEM to characterize the nanostructure evolution of from 600 degrees C to 1300 degrees C. After rapid heating at different temperatures, the silica aerogels were characterized by SEM, BET, TG-DSC, XRD and FT-IR. The nanostructure evolution of the aerogels can be divided into three temperature stages and experimental strategies for inhibiting aerogel shrinkage at high temperature can be provided. In stage I (600 degrees C-1000 degrees C), the shrinkage of the silica aerogels occurred during the initial time of the heating process (within 2 h), and then the structure of silica aerogel became stable. The shrinkage of silica aerogels is primarily caused by the fusion of secondary particles, and increasing the secondary silica aerogel particle size may contribute to reducing the aerogel shrinkage. In stage II (1100 degrees C), the aerogel shrinkage can be observed all the time with the heating process continues, and finally closed to the dense state. The shrinkage of silica aerogels is caused by the fusion of secondary particles and the macropore collapse, increasing the particle size and reducing the macropore content may slow down aerogel shrinkage. In stage III (1200 degrees C-1300 degrees C), the aerogel will shrink rapidly and reach a dense state in a very short time (within 0.5 h). The shrinkage of silica aerogels is caused by the rapid pore collapse and the rapid fusion and shrinkage of the secondary particles of the aerogel, and pure silica aerogels cannot be used at this temperature.