Abstract:In order to have a better understanding of the fracture mechanisms of body-centered-cubic (bcc) metal, the multiscale quasi-continuum method (QC) was employed to analyze the nano-sized crack of bcc tungsten. The mode II crack of tungsten (W) in {110} planes along the [111] direction was simulated. The load-displacement curve and atom displacement images for each loading step were presented. The generation of partial dislocations, the nucleation and emission of perfect dislocations and the movement of dislocations in crack tip were observed. Simulation results show that partial dislocations will produce before perfect dislocation nucleation; each drop point of the load-displacement curve corresponds to the nucleation and emission of a perfect dislocation; dislocation nucleation happens several times along with the dislocation launching; the increasing number and rapid movement of dislocations eventually lead to mode II fracture. According to the simulation results, the curve of dislocation position vs displacement was presented, and the movement characteristics of dislocations were analyzed. The results show that all the dislocations will launch after a new dislocation nucleation, indicating that a new dislocation nucleation will promote dislocation movement, and dislocation movement will speed up with the increase in the number of dislocations. In addition, the phenomenon and mechanism of dislocation in bcc metal was analyzed according to the theory of crystallology and Rice' theory of unstable stacking fault energy. Finally, the forces on and between dislocation were discussed. By calculating the force balance equation in microscale, the initial equilibrium position of the dislocation was forecasted, and the movement mechanism of dislocations near the crack tip was explained, which coincides well with the simulation results.

Multiscale Simulation of Mode II Atomistic Crack in BCC Tungsten