Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Preparation and Properties of Yf3:Eu3+ Luminescent Nanobundles by Hydrothermal Method

Facile Synthesis and Luminescence Properties of Uniform and Well-Dispersed Yf3:Eu3+ Architectures

Synthesis and Luminescence Properties of Lanthanide (Iii)-Doped YF3 Nanoparticles

Hydrothermal Synthesis and Luminescence Properties of NaGdF4:Eu3+ Crystals

Synthesis and Luminescence Properties of GdF3:Ce3+, Ln(3+)(Ln(3+)=Eu3+, Tb3+, Dy3+, Sm3+) Nanocrystals

Luminescence Behavior of Eu3+ Doped LaF3 Nanoparticles.

Synthesis and Luminescence Behavior of Eu3+-doped CaF2 Nanoparticles

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Hydrothermal Synthesis and Luminescent Properties of CexGd1−xF3:Ln3+nanocrystals

Structure and Spectral Properties of NaY<sub>2</sub>F<sub>7</sub>:Eu<SUP>3+</SUP>/Eu<SUP>2+</SUP> Transparent Glass-Ceramics

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Effect of Eu3+ doping concentration on the structural and luminescence properties of NaYF4: Eu3+ nanoparticles

Hydrothermal Synthesis and Luminescence of Eu-Doped Ba<sub>0.92</sub>Y<sub>2.15</sub>F<sub>8.29</sub>Submicrospheres

Uniform Yf3 Nanorods: Synthesis, Luminescent Properties and Cytotoxicity Study

Preparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires

Synthesis and Photoluminescent Properties of NaYF<SUB>4</SUB>:Eu<SUP>3+</SUP> Core and NaYF<SUB>4</SUB>:Eu<SUP>3+</SUP>/NaYF<SUB>4</SUB> Core/Shell Nanocrystals

Synthesis and Tunable Photoluminescence of NaYF4:Eu/Ba Nanocrystals

Monodisperse Mesocrystals of Yf3 and Ce3+/Ln3+(Ln=Tb, Eu) Co-Activated Yf3: Shape Control Synthesis, Luminescent Properties, and Biocompatibility

Facile Synthesis and Luminescence Properties of Octahedral Yvo4:Eu3+ Microcrystals

Facile Synthesis of Lanthanide (ce, Eu, Tb, Ce/Tb, Yb/Er, Yb/Ho, and Yb/Tm)-Doped LnF3 and LnOF Porous Sub-Microspheres with Multicolor Emissions.

Synthesis and Properties of Europium-Based Phosphors on the Nanometer Scale: Eu2O3, Gd2O3:Eu, and Y2O3:Eu.