Understanding grain refinement of Sc addition in a Zr containing Al-Zn-Mg-Cu aluminum alloy from experiments and first-principles
Yu Liu,Chuan-Chao Zhang,Xie-Yi Zhang,Yuan-Chun Huang
DOI: https://doi.org/10.1016/j.intermet.2020.106823
IF: 4.075
2020-08-01
Intermetallics
Abstract:<p>In this work, we present a better insight into the grain refining mechanism of Sc addition in an Al-Zn-Mg-Cu-Zr aluminum alloy from experiments and first-principles. It is found a higher concentration of Sc can result in finer grains, but the refining efficiency was sharply decreased when the Sc/Zr ratio(wt.%) exceeds 1. Also, we determined the L1<sub>2</sub>-Al<sub>3</sub>(Sc, Zr) was formed by Sc displacing Zr in L1<sub>2</sub>-Al<sub>3</sub>Zr, and those generated particles distributed around L1<sub>2</sub>-Al<sub>3</sub>Zr. Moreover, the content of Zr was found overwhelmed by Sc within a Sc and Zr containing particle in high Sc/Zr ratio alloys. The calculated surface energy indicates a low Sc doping (<21.4 at.%) tends to stabilize L1<sub>2</sub>-Al<sub>3</sub>Zr(111) surface, when the doping content in the range of 21.4–35.7%, the clean L1<sub>2</sub>-Al<sub>3</sub>Zr(111) is energetically favored, when the doping content is higher than 35.7%, the L1<sub>2</sub>-Al<sub>3</sub>(Sc, Zr)(111) is preferred. Based on the interface energy, the capability of heterogeneous nucleation to α-Al can be ordered as L1<sub>2</sub>-Al<sub>3</sub>(Sc, Zr) > L1<sub>2</sub>-Al<sub>3</sub>Zr > L1<sub>2</sub>-Al<sub>3</sub>Sc. However, in a Sc rich condition, the formation of L1<sub>2</sub>-Al<sub>3</sub>(Sc, Zr)(111) and Al(111)/L1<sub>2</sub>-Al<sub>3</sub>(Sc, Zr)(111) interface were hindered by the formation of L1<sub>2</sub>-Al<sub>3</sub>Sc(111), thus, further refinement of grains was limited, the results well explained the experimental observations.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering