Abstract:The development of noble metal catalysts with high catalytic performance and low metal loading has attracted much interest. However, the separation of the used nanoscale catalyst from the process is challenging. Most of the separation system, such as resin or membrane leads to a sacrifice of high surface area as well as catalytic efficiency. Herein, two series of recyclable catalysts were synthesized by loading palladium (Pd) particles onto melamine formaldehyde (MF) modified cellulose nanocrystals (CNC) and dopamine (DA) coated CNC. In situ co-precipitation of magnetic nanoparticle (MNP) clusters were used to impart magnetic characteristic to the catalysts. This magnetic cluster successfully achieved high magnetization without aggregation. The amount of palladium precursor added to the catalytic systems was optimized, where 10-Pd-PDC yielded 10.83 ± 2.43 nm discrete Pd loaded hybrids. The catalytic performance was assessed by the reduction of 4-nitrophenol (4-NP) in the presence of sodium borohydrides (NaBH 4 ). The 4-NP reduction mechanisms were analyzed using the Langmuir-Hinshelwood model and the apparent rate constant k (s −1 ), turnover frequency (TOF, h −1 ) and activity factors (s −1 g −1 ) were determined to be 2.142 × 10 −3 , 305.82 and 535.5 using MNP2-Pd-MC respectively. An induction time was observed for MNP4 or 5-Pd-PDC, which was attributed to the unignitable diffusion time for reagents to cross the thick PDA and MNP layer. The separation efficiency of the magnetic catalysts was evaluated by monitoring the absorbance at 400 nm as a function of separation time, and the MNP2-Pd-MC could be recycled 7 times without severe loss. Pd-MF-CNC displayed excellent catalytic performance for the reduction of 4-NP, while Pd-PDA-CNC possessed an inferior catalytic reactivity due to the reduced catalytic surface area. The developed templated MNP could be extended to other systems allowing for the recycling and reuse of the catalysts.

The Preparation of Hollow Fe3O4/Pd@C NCs to Stabilize Subminiature Pd Nanoparticles for the Reduction of 4-Nitrophenol

High-performance Cu Nanoparticles/three-Dimensional Graphene/ni Foam Hybrid for Catalytic and Sensing Applications.

Pd nanoparticles anchored Co-MOF for nitrophenol reduction

In Situ Growth of Pd Nanosheets on g-C3 N4 Nanosheets with Well-Contacted Interface and Enhanced Catalytic Performance for 4-Nitrophenol Reduction.

Pd/N-doped carbon dots@dendritic mesoporous silica nanospheres: A highly efficient catalyst for the hydrogenation of 4-nitrophenol

Preparation of magnetically separable and low-cost MC-FePd3 NPs with enhanced catalytic activity in the reduction of p-nitrophenol

Salivary duct adenocarcinoma

A novel magnetic cluster modified palladium-cellulose nanocrystal hybrids as recyclable catalyst for 4-nitrophenol reduction

Deposition of Pd on Co(OH)2 nanoplates in stabilizer-free aqueous phase for catalytic reduction of 4-nitrophenol

High-Performance Catalytic Reduction of 4-Nitrophenol to 4-Aminophenol over Pt Nanoparticles Supported on Co-Al LDH Nanosheets

Fock-space coupled-cluster method: The (1,2) sector.

Efficient Reduction of 4-Nitrophenol Catalyzed by 4-Carbo-methoxypyrrolidone Modified PAMAM Dendrimer–silver Nanocomposites

In-situ synthesis of ultrafine Co nanoparticles confined in interconnected nitrogen-doped carbon networks for enhanced reduction of 4-nitrophenol

Promotional effect of embedded Ni NPs in alginate-based carbon toward Pd NPs efficiency for high-concentration p-nitrophenol reduction

Pd–Fe bimetallic nanoparticles anchored on N-doped carbon-modified graphene for efficient catalytic organic reactions

In-situ fabrication of Fe3O4@C/Pt nanocomposite and investigation of its catalytic activity

Magnetic Pd/Fe3O4 Composite: Synthesis, Structure, and Catalytic Activity

Amphiphilic Dendronized Copolymer-Encapsulated Au, Ag and Pd Nanoparticles for Catalysis in the 4-Nitrophenol Reduction and Suzuki–Miyaura Reactions

CoFe Nanoparticle-Decorated Reduced Graphene Oxide for the Highly Efficient Reduction of 4-Nitrophenol

Palladium-Decorated Covalent Organic Framework Supported on Zinc Ferrite as Magnetic Catalyst for Suzuki Reaction and p-nitrophenol Reduction

Metallic CoNi nanoparticles anchored on heteroatoms doped Carbon/MnO nanowires for improved catalytic performance