Abstract:A new potassium-based adsorbent for CO2 capture with Al aerogel used as support is proposed in this work. The adsorbents with different surface modifiers (tetraethyl orthosilicate (TEOS) and trimethyl chlorosilane (TMCS)) and different K2CO3 loadings (10%, 20%, 30% and 40%) were prepared by sol-gel and iso-volume impregnation processes with ambient pressure drying. The CO2 adsorption performance of the adsorbents were tested by a fixed-bed reactor, and their adsorption mechanisms were studied by scanning electron microscopy (SEM), Brunauer Emmett Teller (BET), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, and X-ray fluorescence spectrometry (XRF). Furthermore, the adsorption kinetics and the cycling performance were investigated. The results show that using TEOS to modify the wet gel can introduce SiO2 to increase the strength of the skeleton. On the basis of TEOS modification, TMCS can further modify –OH, thus effectively avoiding the destruction of aerogel structure during ambient drying and K2CO3 impregnation. In this work, the specific surface area and specific pore volume of Al aerogel modified by TEOS + TMCS are up to 635.32 cm2/g and 2.43 cm3/g, respectively. The aerogels without modification (Al-B), TEOS modification (Al/Si) and TEOS + TMCS modification (Al/Si-TMCS) showed the best CO2 adsorption performance at 20%, 30% and 30% K2CO3 loading, respectively. In particular, the CO2 adsorption capacity and K2CO3 utilization rate of Al/Si-TMCS-30K are as high as 2.36 mmol/g and 93.2% at 70 degrees Celsius (°C). Avrami’s fractional order kinetic model can well fit the CO2 adsorption process of potassium-based adsorbents. Al-B-20K has a higher apparent activation energy and a lower adsorption rate during the adsorption process. After 15 adsorption-regeneration cycles, Al/Si-TMCS-30K maintain a stable CO2 adsorption capacity and framework structure, while the microstructure of Al/Si-30K is destroyed, resulting in a decrease in its adsorption capacity by nearly 30%. This work provides key data for the application of Al aerogel in the field of potassium-based adsorbent for CO2 capture.

Carbonation and Active-Component-Distribution Behaviors of Several Potassium-Based Sorbents

Properties of a Nano CaO/Al2O3 CO2 Sorbent

Study on the kinetics of Ca-based CO2 sorbent of carbonation and calcination for adsorption enhanced reforming process

Thermogravimetric analysis of carbonation behaviors of several potassium-based sorbents in low concentration CO2

Kinetic Analysis of an Anion Exchange Absorbent for Co2 Capture from Ambient Air

Reaction mechanism of dry potassium-based solid sorbent for CO2 capture in confined spaces at ambient temperature

Porosity and Hydrophilicity Modulated Quaternary Ammonium-Based Sorbents for CO2 Capture

Effect of K2CO3·1.5H2O on the Regeneration Energy Consumption of Potassium-Based Sorbents for CO2 Capture

Carbonation Behavior of K2CO3/AC in Low Reaction Temperature and CO2 Concentration

Properties of a Nano CaO/Al<sub>2</sub>O<sub>3</sub>CO<sub>2</sub>Sorbent

Removal of Low Concentration Co2 at Ambient Temperature Using Several Potassium-Based Sorbents

CO2 Sorption and Reaction Kinetic Performance of K2CO3/AC in Low Temperature and CO2 Concentration

Cost-effective carbon-based amine adsorbents for carbon capture: Equilibrium, kinetics and selectivity

K2co3-Modified Potassium Feldspar for Co2 Capture from Post-Combustion Flue Gas

Resorcinol–formaldehyde Resin-Based Porous Carbon Spheres with High CO2 Capture Capacities

K2CO3-Impregnated Al/Si Aerogel Prepared by Ambient Pressure Drying for CO2 Capture: Synthesis, Characterization and Adsorption Characteristics.

Modeling of the Carbonation Kinetics of A Synthetic Cao-Based Sorbent

Novel Fluidizable K-Doped HAc-Li4SiO4 Sorbent for CO2 Capture Preparation and Characterization

Kinetics of removal of CO2 by calcium-based sorbents

Carbonation Kinetics of CO2 with CaO-Ca9Al6O18 Sorbent

Self-Activation Mechanism Investigations on Large K2co3-Doped Li4sio4 Sorbent Particles