Regulation of Pore Structure and Acidity of a ZSM-5 Catalyst for Dehydration of Glycerol to Acrolein
Pan Wen-Ya,Huang Liang,Qin Feng,Zhuang Yan,Li Xue-Mei,Ma Jian-Xue,Shen Wei,Xu Hua-Long
DOI: https://doi.org/10.3866/pku.whxb201503024
2015-01-01
Abstract:Pore structure and acidity of ZSM-5 catalysts were successfully regulated by alkali treatment. ZSM5 was etched in 0.2 mol . L-1 NaOH solution at 65 and 85 degrees C. Micro-mesoporous ZSM-5 catalysts were successfully prepared with a high density of acidic sites. The activity and stability were significantly enhanced with alkali-treated ZSM-5, giving a conversion of glycerol above 95%, with selectivity for acrolein of 78% after 10 h compared with a ZSM-5-at85 (alkali-treated at 85 degrees C) catalyst. Characterization of N-2 adsorption and desorption isotherms, X-ray diffraction (XRD), Al-27 mass atomic spectroscopy-nuclear magnetic resonance (Al-27 MAS-NMR), and transmission electron microscopy (TEM) were performed to interpret the morphology and surface properties. The results reveal that the Si in the framework of ZSM-5 was leached out by alkali treatment, and many mesopores were formed on the ZSM-5 surface. However, the MFI topology did not change and Al was mainly integrated within the framework. X-ray photoelectron spectroscopy (XPS), X-ray fluorescence (XRF), and NH3-temperature-programed desorption (NH3-TPD) experiments demonstrated that the molar ratio of Si! Al on the external surface was lower than that in the framework, indicating that more Si on the external surface of ZSM-5 was leached by alkali treatment, while the acidic density increased because of the lower molar ratio of Si/Al near newly formed mesopores. ZSM-5 catalysts with mesopores and higher acidic density enhance reactant diffusion and coking tolerance, which improves the activity and stability during glycerol dehydration.