Mechanism Study on the Asymmetric Behaviors of Carbon/Carbon Supercapacitors
Lintong Hu,Huiqiao Li
DOI: https://doi.org/10.1149/ma2016-02/7/1035
2016-01-01
ECS Meeting Abstracts
Abstract:Electrical double layer capacitors (EDLCs) have attracted tremendous attention for their high power density, long cycle life, excellent stability and fast charge-discharge rate. Due to the high surface area, good conductivity, and high chemical stability in different solutions, many efforts are devoted to explore carbon-based materials for EDLCs. However, a common phenomenon that the positive and negative electrodes have unequal capacitance in carbon/carbon supercapacitors has not received the deserved attention. [1, 2] The asymmetric capacitance limits the potential window and hence the cell energy density. [3,4] By smart balancing the asymmetric behaviors of the positive and negative electrodes, a higher energy density can be expected for supercapacitors without additional cost. Thus the mechanism study on the asymmetric phenomenon is of great meaning to achieve high performance supercapacitors. We studied the capacitive behaviors of the positive and negative electrode in a carbon/carbon supercapacitor respectively by using both experimental measurements and molecular dynamics calculations. Two different electrolytes, tetraethylammonium tetrafluoroborate (TEABF4) and lithium hexafluorophosphate (LiPF6) in propylene carbonate (PC), were used for the identical carbon electrodes. Cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD) tests show that the two electrodes in a capacitor not only exhibit different specific capacitance but also work in different width of voltage window. Theoretical calculations give a full explanation of the experiment observations, which indicate that the size of solvated ions, the diffusion property and the solvation energy play important roles in such asymmetric behaviors. The results help to get a deep understanding of factors involved in the charge storage mechanism and can provide guidance for designing appropriate carbon-electrolyte system for EDLCs. References [1] Chmiola, J.; Largeot, C.; Taberna, P. L.; Simon, P.; Gogotsi, Y.; Angew. Chem. Int. Ed. 2008, 47, 3392. [2] Wang, H.; Forse, A. C.; Griffin, J. M.; Trease, N. M.; Trognko, L.; Taberna, P. L.; Simon, P.; Grey, C. P.; J. Am. Chem. Soc. 2013, 135, 18968. [3] Weng, Z.; Li, F.; Wang, D. W.; Wen, L.; Cheng, H. M.; Angew. Chem. Int. Ed. 2013, 52, 3722. [4] Aken, K. L. V.; Beidaghi, M.; Gogotsi, Y.; Angew. Chem. Int. Ed. 2015, 54, 4806-4809. Figure 1