Abstract:In the development of water splitting, the sluggish electrocatalytic kinetics of the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) have restricted their energy conversion efficiencies. Along with the continuous rise in the prices of noble metals and transition metals (such as cobalt and nickel), constructing high-efficiency HER/OER catalysts based on low cost transition metals, such as iron and manganese, is becoming more meaningful in developing industrialized water splitting devices. In this paper, in the absence of a template or active agent, three-dimensional, hierarchically porous FexMny nanoparticles (NPs) were embedded and nitrogen-doped carbon materials (denoted as FexMny@NC; x:y, representing the molar ratio of Fe:Mn) were successfully prepared via pyrolysis of corresponding precursors containing different metallic salt components. Various morphological, structural, and chemical characterization analysis demonstrate that at an Fe:Mn molar ratio of 3:1, the optimal Fe3Mn1@NC material shows high graphitization degree, rich mesoporous structures, a large surface area, and abundant carbon defects/edges, which promote the uniform dispersion of pyridinic-N (pyridinic-N-metal), graphitic-N, carbon oxygen bonds (C–O), manganese oxide (MnO) nanocrystals, and Fe3C NPs-embedded, N-doped carbon sheet (Fe3) active sites. In alkaline conditions, the HER onset potentials (Eonset) and potentials recorded at 10 mA cm-2 (E10) of the optimal Fe3Mn1@NC are just 84.8 and 156 mV more negative than those of 20 wt% platinum carbon (Pt/C). Meanwhile, the OER Eonset and E10 values of the optimal Fe3Mn1@NC are just 8 and 18.7 mV more positive than those of RuO2. Furthermore, optimized Fe3Mn1@NC catalysts were assembled into a water splitting cell, where the catalytic current density achieves 10 mA cm-2 at a low voltage of 1.6287 V (with superior catalytic stability), which is just 24.9 mV higher than that of the (-) 20 wt% Pt/C||RuO2 (+) benchmark (1.6038 V) under the same conditions. This work describes the regulating efficiency of Mn toward growing mesopores and opens new possibilities for the development of novel carbonaceous catalysts with excellent hydroxide catalytic efficiencies based on low cost Mn/Fe elements.

Boosting the Catalytic Performance of Iron Phosphide Nanorods for the Oxygen Evolution Reaction by Incorporation of Manganese

Cobalt And Vanadium Co-Doped Feooh Nanoribbons: An Iron-Rich Electrocatalyst For Efficient Water Oxidation

Ni 2– x Mn x P Nanoparticles as Earth-Abundant Precatalysts for Electrochemical Water Oxidation

Morphological modulation of iron carbide embedded nitrogen-doped hierarchically porous carbon by manganese doping as highly efficient bifunctional electrocatalysts for overall water splitting

Two‐Phase Colloidal Synthesis of Amorphous Iron‐Doped Manganese Phosphate Hollow Nanospheres for Efficient Water Oxidation

Constructing sulfide/phosphide heterostructure boosts the activity of iron-manganese bimetallic electrocatalysts for oxygen evolution reaction at large current densities

Rational design of bimetal phosphide embedded in carbon nanofibers for boosting oxygen evolution

Ultrafine Bimetallic Phosphide Nanoparticles Embedded in Carbon Nanosheets: Two-Dimensional Metal-Organic Framework-Derived Non-Noble Electrocatalysts for the Highly Efficient Oxygen Evolution Reaction

Superlattice-Like Co-Doped Mn Oxide and NiFe Hydroxide Nanosheets toward an Energetic Oxygen Evolution Reaction

Two-Dimensional Bimetallic Phosphide Ultrathin Nanosheets As Non-Noble Electrocatalysts For A Highly Efficient Oxygen Evolution Reaction

Sulfur, phosphorus and iron codoped nickel oxide as an efficient catalyst for the oxygen evolution reaction

Highly Efficient Oxygen Evolution Reaction Enabled by Phosphorus Doping of the Fe Electronic Structure in Iron–Nickel Selenide Nanosheets

Iron, manganese co-doped Ni3S2 nanoflowers in situ assembled by ultrathin nanosheets as a robust electrocatalyst for oxygen evolution reaction

Porous Mn-doped cobalt phosphide nanosheets as highly active electrocatalysts for oxygen evolution reaction

High-valence-state Ni–Fe bimetallic phosphonate nanoribbons catalyst for enhanced photocatalytic and electrocatalytic oxygen production

Modulating electronic structure of Ni2P pre-catalyst by doping trace iron for enhanced oxygen evolution reaction in alkaline

Bimetal synergistically regulates Ni and P oxidation states for efficient oxygen evolution reaction

An Efficient Bio-inspired Oxygen Reduction Reaction Catalyst: MnO X Nanosheets Incorporated Iron Phthalocyanine Functionalized Graphene

Chemical Transformation Induced Core–Shell Ni2P@Fe2P Heterostructures toward Efficient Electrocatalytic Oxygen Evolution

Hierarchical Highly Wrinkled Trimetallic NiFeCu Phosphide Nanosheets on Nanodendrite Ni3S2/Ni Foam As an Efficient Electrocatalyst for the Oxygen Evolution Reaction.

Manganese Oxide as an Inorganic Catalyst for the Oxygen Evolution Reaction Studied by X‐Ray Photoelectron and Operando Raman Spectroscopy