Ultra-broadband Near-Infrared Photoluminescence in Er3+-Ni2+co-doped Transparent Glass Ceramics Containing Nano-Perovskite KZnF3

Xin Wang,Pengfei Wang,Haiyan Zhao,Ke Tian,Shijie Jia,Shunbin Wang,Gilberto Brambilla

DOI: https://doi.org/10.1016/j.ceramint.2020.07.088

IF: 5.532

2020-01-01

Ceramics International

Abstract:In this article, ultra-broadband photoluminescence in near-infrared is achieved in KZnF3 glass ceramics doped with Er3+ and Ni2+ ions. Er3+ -Ni2+ co-doped fluorosilicate glass and glass ceramics embedded with perovskite nanocrystals were fabricated and efficient energy transfer (ET) from Er3+ to Ni2+ ions was confirmed by luminescence spectra and decay curves. In the glass ceramic samples, Ni2+ ions were effectively sensitized by Er2+, and ultra-broadband photoluminescence from 1400 to 2300 nm was observed when a 980 nm laser was used as a pump, as shown in Fig. 1. The temperature and humidity stability of the glass ceramic samples was characterized from the measured transmittance. These results demonstrated that Ni2+ -Er3+ co-doped glass ceramics have significant potential for application in optical communication and broadband amplifiers.