Self-assembly Behavior of Amino Modified Cellulose Nanocrystals

Li-sha Yu,Yan-hui Kang,Chen He,Jin-ping Zhou

DOI: https://doi.org/10.11777/j.issn1000-3304.2020.20069

2020-01-01

Acta Polymerica Sinica

Abstract:Cellulose nanocrystals (CNCs) are a class of sustainable renewable nanomaterials with many advanced features, such as biodegradability, biocompatibility, large specific surface area, and outstanding mechanical properties. They have attracted significant interest due to their fascinating self-assembly behavior. In this work, amino modified CNCs (CNC-NH2) were prepared by reacting CNCs with epichlorohydrin and then with ammonia. The structure, morphology and self-assembly behavior of CNCNH2 in aqueous suspensions and solid films were investigated by UV-Vis spectroscopy, DLS, XRD, XPS, POM, AFM, SEM, TEM and rheology testing. The degree of substitution of amino groups was deternmined to be 0.048. CNC-NH2 showed a rodlike morphology with the length (L) of (180 +/- 75) nm and width (W) of (13 +/- 5) nm, and the average aspect ratio (L/W) was nearly 13.8. CNC-NH2 could be well dispersed in water and the zeta-potential was determined to be -28.0 mV, which could be stored for a long time due to the strong electrostatic repulsion. The chiral nematic liquid crystal was observed in the CNC-NH2 suspensions as the solid content increased up to 1.75 wt%. The CNC-NH2 suspensions displayed unique rheological properties, which were divided into three regions: isotropic, biphase and liquid crystal, with increasing solid content. Moreover, the evaporation-induced self-assembly (EISA) method was used to prepare CNC-NH2 films. It was found that the liquid crystalline structure of CNC-NH2 in colloidal suspension still maintained in the solid films. The iridescent color of the films could be tuned by the initial content of the suspension and the ultrasonic time. The iridescence and colored films were obtained only if the pitch length in the solid film was approximately that of the wavelength of visible light. This work provides a new way for the preparation of cellulose liquid crystal materials, and helps to understand the formation mechanism of the liquid crystal of the rodlike nanoparticles.