White Up-conversion Emission of Hydrothermally Synthesized Hexagonal NaYbF4∶Er3+/Tm3+
Li-fang LIANG,Jian-le ZHUANG,Hao WU,Jing WANG,Ming-mei WU,Qiang SU
2008-01-01
Chinese Journal of Luminescence
Abstract:Over the past decades,there has been a significant interest in the production of new materials for multicolor displays.A new technique for solid-state color displays has been developed based upon infrared to visible frequency upconversion in lanthanide doped materials.The three primary colors red,green and blue can be obtained from upconversion luminescence of Er3+,Pr3+,Ho3+ and Tm3+ etc.However the relative intensities of the three primary colors are still required to control.Thus,it is necessary to develop novel mate-rials capable of multicolor upconversion and investigate their upconversion mechanisms of rare earth ions employed.Rare earth doped fluoride crystals is one of the most attractive materials for near-infrared to visible upconversion because its low phonon energies.In this work,we present intense multicolor upconversion luminescence in Er3+/Tm3+ codoped NaYbF4.The relation between upconversion intensity of three fundamental colors and the dopant concentration was discussed and the corresponding upconversion mechanism was proposed.The generation and control of the primary colors through upconversion of Tm3+ and Er3+ in NaYbF4 with single excitation(980 nm)were obtained.The hexagonal NaYbF4∶Er3+,NaYbF4∶Tm3+,NaYbF4∶Er3+/Tm3+ upconverting phosphors have been prepared by hydrothermal method under 220 ℃ for 48 h.The crystal structure and luminescent properties were investigated by using powder X-ray diffraction,diffuse reflectance absorption spectra and fluorescent spectra.The result of powder XRD spectra reveals that Er3+ and Tm3+ ions can incorporate completely into hexagonal NaYbF4 lattice at any concentration by mild hydrothermal method.The diffuse reflectance absorption spectra shows that the absorption peak band centered at 957 nm corresponds to 2F7/2→2F5/2 transition of Yb3+ ion for NaYbF4,and the absorption peaks of NaErF4 or NaTmF4 could be assigned to the transitions from ground state of Er3+(4I15/2)or Tm3+(3H6)to excited states.Under 980 nm excitation,hexagonal NaYbF4∶Er3+ can emit strong green and,red emission,which correspond to(2H11/2,4S3/2)→4I15/2,4F9/2→4I15/2 transition of Er3+,respectively.NaYbF4∶Tm3+ exhibit intense blue upconversion emission,which is attributed to 1D2→3F4 and 1G4→3H6 transition of Tm3+.The emission intensity of blue transitions(1G4 →3H6,1D2→3F4)is enhanced considerably as increasing Yb3+ content and reach the optimum at NaYbF4∶Tm3+.We agree with the view that the excitation is mobile within the NaYbF4 lattice,it could thus readily reach the Tm3+ traps,which cause the high relative intensity of the two blue emissions(1G4→3H6,1D2→3F4).Tm3+ and Er3+ ions can be easily codoped in NaYbF4 lattice through the mild hydrothermal route,and an energy transfer between Tm3+ and Er3+ exists under 980 nm laser excitation:1D2(Tm3+)+4I15/2(Er3+)→ 3F4(Tm3+)+ 4S3/2 or 2H11/2(Er3+),1G4(Tm3+)+ 4I15/2(Er3+)→3H6(Tm3+)+ 4S3/2 or 2H11/2(Er3+).The relative ratio of green,red and blue emission intensity can be tuned by defining Tm3+ and Er3+ ion concentration in the NaYbF4 lattice,and through which,a white light simulation could be obtained in the Tm3+ and Er3+ codoped NaYbF4.