Abstract:In this dissertation, the relationships between structure-mechanical properties-deformation mechanisms in face-centered cubic (FCC) and body-centered cubic (BCC) metallic nanowires have been studied using in situ TEM nanomechanical testing. It is well known that smaller is stronger and the widely-observed size effect is believed to arise from dislocation interactions inside nanocrystals. However, the interaction mechanisms in small-volume nanocrystals remain unexplored. Here, it was found that surface-nucleated dislocations can strongly interact inside the confined volume of Au nanowires, which led to a new type of dislocation-originated stacking fault tetrahedra (SFT), at variance to the widely-believed vacancy-originated SFT. The atomic-scale processes of nucleation, migration and annihilation of dislocation-originated SFT were revealed, shedding new light onto the strain hardening and size effect in small-volume materials. Although nanoscale twinning is an effective mean to enhance the strength of metals, twin-size effect on the deformation and failure of nanotwinned metals remains largely unexplored, especially at the minimum twin size. Here, a new type of size effect in nanotwinned Au nanowires is presented. As twin size reaches the angstrom-scale, Au nanowires exhibit a remarkable ductile-to-brittle transition that is governed by the heterogeneous-to-homogeneous dislocation nucleation transition. Quantitative measurements show that approaching such a nanotwin size limit gives rise to the ultra-high strength in Au nanowires, close to the ideal strength limit of perfect Au. Twinning is a fundamental deformation mode that competes against dislocation slip in crystals. At the nanoscale, higher stresses are required for plastic deformation than that in bulk, which favors twinning over dislocation slip. Indeed, deformation twinning has been well-documented in FCC nanocrystals. However, it remains unexplored in BCC nanostructures. Here, it shows that twinning is the dominant deformation mode in BCC-tungsten nanocrystals. A competition between twinning and dislocation slip occurs when changing the loading orientations, attributed to the defect growth controlled plasticity in BCC nanocrystals. Several important commonalities and differences in FCC and BCC nanocrystals deforming at nanoscale are further proposed. The results from this dissertation advance fundamental understanding of plastic deformation in a broad class of metals and alloys, and are of technological importance for degradation control and future design of ultra-strength nanomaterials.

A NEW PERSPECTIVE ON NANO-MECHNICS: QUANTITATIVE DEFORMATION TEST IN THE TEM

Atomistic perspective on in situ nanomechanics

In Situ TEM Study on the Nanomechanical Behaviors of Metallic Nanowires

In Situ Nanomechanical Testing of Twinned Metals in a Transmission Electron Microscope

A New Perspective on Mechanical Testing: in Situ Compression in the TEM

Nanoscale compression testing inside a TEM

In Situ Experimental Mechanics of Nanomaterials at the Atomic Scale

Plasticity live: Direct observation nanomechanical testing in the TEM

In Situ TEM Investigation of the Mechanical Behavior of Micronanoscaled Metal Pillars

In Situ Tem Nanomechanics

Microelectromechanical System for in Situ Quantitative Testing of Tension-Compression Asymmetry in Nanostructures

Mechanical Annealing and Source-Limited Deformation in Submicrometre-Diameter Ni Crystals

B11-O-10In Situ Atomic Scale Mechanical Microscopy

Advances in Understanding Atomic-Scale Deformation of Small-Sized Face-Centered Cubic Metals with in Situ Transmission Electron Microscopy

Insights into fundamental deformation processes from advanced in situ transmission electron microscopy

Atomic-Scale-Deformation-Dynamics (asds) of Nanowires and Nanofilms

Nano-Scale Testing of Nanowires and Carbon Nanotubes Using a Micro-Electro-Mechanical System

<i>In situ</i> characterization of the mechanical properties of nanoparticles and nanoscale structures

B12-O-19 Real-time Atomistic Observation of the Mechanical Deformations in Au Nanostructures

MS-10-IN-6086 Crossover Plasticity Mechanisms in Nano Single- and Polycrystalline Metals: By in situ atomic scale mechanical microscopy

Atomic-scale observation of the deformation and failure of diamonds by in-situ double-tilt mechanical testing transmission electron microscope holder