Abstract:In this work an intercalation-chemistry-based method to synthesize tungstate and tungsten oxide nanosheets was described. A layered bismuth tungstate (Bi2W2O9) was used as the W-containing starting material. After the bismuth oxide layers were leached by a chloride acid, a protonated form, H2W2O7 center dot xH(2)O with sizes of 5-15 mu m, was achieved. The intercalation reaction of n-octylamine with H2W2O7 center dot xH(2)O in heptane and the subsequent dissolution-recrystallization process led to the formation of tungstate-based inorganic organic hybrid nanobelts. Orthorhombic WO3 center dot H2O nanosheets were obtained by removing the organic species of the as WO3 center dot H2O nanosheets at 250-450 degrees C, monoclinic WO3 nanosheets were achieved. The results of XRD, TEM and SEM indicate that the obtained WO3 center dot H2O and WO, were single-crystalline nanosheets with areas of (200-500) nm x (200-500) nor and thicknesses of 10-30 nm. The SAED patterns suggest that the WO3 center dot H2O and WO3 nanosheets possessed a reduced directions of [010] and [001], respectively. N-2 adsorption measurement results indicate that the specific surface areas of the as-obtained WO3 center dot H2O and WO3 nanosheets were up to 250 and 180 m(2)/g, respectively. The formation mechanisms for hybrid nanobelts, WO3 center dot H2O and WO3 nanosheets were discussed. The proposed novel route was efficient in producing two-dimensional WO3 nanosheets on a large scale.

Syntheses and Mechanism of Wo3 Center Dot H2o Nanoflowers Assembled of Square Nanoplates with the Assistance of Oxalic Acid

Oxalic Acid Mediated Synthesis of WO3·H2O Nanoplates and Self-Assembled Nanoflowers under Mild Conditions

Synthesis and controlled growth of monodisperse WO3· H2O square nanoplates with the assistance of malic acid

Controllability of Assemblage from WO3·H2O Nanoplates to Nanoflowers with the Assistance of Oxalic Acid

Novel Route to WO<i><sub>x</sub></i>Nanorods and WS<sub>2</sub>Nanotubes from WS<sub>2</sub>Inorganic Fullerenes

WO3 Nanostructures Synthesized by a Sonochemical Strategy

Novel route to WOx nanorods and WS2 nanotubes from WS2 inorganic fullerenes.

Hydrothermal Synthesis And Gas Sensing Properties Of Wo3 Center Dot H2o With Different Morphologies

Tungstenic acid induced assembly of hierarchical flower-like MoS2 spheres

Green Synthesis Of Hexagonal-Shaped Wo3 Center Dot 0.33h(2)O Nanodiscs Composed Of Nanosheets

Synthesis of Uniform WO3 Square Nanoplates Via an Organic Acid-Assisted Hydrothermal Process

Synthesis, characterization and formation mechanism of single-crystal WO 3 nanosheets via an intercalation-chemistry-based route

Synthesis, Characterization and Formation Mechanism of Single-Crystal Wo3 Nanosheets Via an Intercalation-Chemistry-Based Route

A Dissolution‐Regeneration Route to Synthesize Blue Tungsten Oxide Flowers and their Applications in Photocatalysis and Gas Sensing

Morphology-controlled WO3−x homojunction: hydrothermal synthesis, adsorption properties, and visible-light-driven photocatalytic and chromic properties

Controlled Synthesis Of Monodisperse Wo3 Center Dot H2o Square Nanoplates And Their Gas Sensing Properties

Microwave-assisted Solvothermal Synthesis and Growth Mechanism of WO3·(H2O)0.33hierarchical Microstructures

WO3·0.33H2O Nanoplates: Hydrothermal Synthesis, Photocatalytic and Gas-Sensing Properties

Large scale hydrothermal synthesis of monodisperse hexagonal WO 3 nanowire and the growth mechanism

Topochemical Preparation of Wo3 Nanoplates Through Precursor H2wo4 and Their Gas-Sensing Performances

Hydrothermal synthesis and gas sensing properties of WO3H2O with different morphologies