Glassy Materials with Enhanced Thermal Stability

Boolchand P.,Goodman B.

DOI: https://doi.org/10.1557/mrs.2016.300

IF: 5

2017-01-01

MRS Bulletin

Abstract:The nature of glass transitions in chalcogenides and modified oxides depends on the network mean coordination number $\langle r\rangle$ . These display systematic trends when spanning across the three topological phases: flexible, intermediate, and stressed-rigid. Trends in the glass-transition temperature T _g( $\langle r\rangle$ ) show a monotonic increase with $\langle r\rangle$ , but the nonreversing enthalpy of relaxation at T _g, Δ H _nr( $\langle r\rangle$ ), shows a deep- and square-well-like minimum with the walls representing the rigidity and stress transitions with increasing $\langle r\rangle$ , respectively. In the well, the Δ H _nr( $\langle r\rangle$ ) term remains minuscule (∼0) corresponding to the isostatically rigid intermediate phase (IP). The melt fragility index ( m ) shows rather low values, m ( $\langle r\rangle$ ) < 20 for IP compositions, but increases outside the IP. Glass compositions in the IP show absence of network stress, form compacted networks, possess thermally reversing glass transitions, and display high glass-forming tendency—functionalities that have attracted widespread interest in understanding the physics of glasses and applications of the new IP formed.